the 4-nm Fe3O4 nanoparticles are made as follows:12 Fe(acac)3 (2 mmol) was mixed in phenyl ether (20 mL) with 1,2-hexadecanediol (10 mmol), oleic acid (6 mmol), and oleylamine (6 mmol) under nitrogen and was heated to reflux for 30 min. After cooled to room temperature, the dark-brown mixture was treated with ethanol under air, and a dark-brown material was precipitated from the solution. The product was dissolved in hexane in the presence of oleic acid and oleylamine and reprecipitated with ethanol to give 4-nm Fe3O4 nanoparticles.
这就是楼上说的sun shouheng 在JACs上发表的，
返回小木虫查看更多
京公网安备 11010802022153号
the 4-nm Fe3O4 nanoparticles are made as follows:12 Fe(acac)3 (2 mmol) was mixed in phenyl ether (20 mL) with 1,2-hexadecanediol (10 mmol), oleic acid (6 mmol), and oleylamine (6 mmol) under nitrogen and was heated to reflux for 30 min. After cooled to room temperature, the dark-brown mixture was treated with ethanol under air, and a dark-brown material was precipitated from the solution. The product was dissolved in hexane in the presence of oleic acid and oleylamine and reprecipitated with ethanol to give 4-nm Fe3O4 nanoparticles.
这就是楼上说的sun shouheng 在JACs上发表的，
这种文章在数据库中还是很容易搜到的，建议楼主自己去筛选。。
想在粒径为30nm的纳米炭黑表面包覆Fe3O4，用什么方法好呢？
你好，你的这篇文献下不了啊，可以不可以给我发一份啊？谢谢你！
我的邮箱是 smmdcr@163.com