没有做过。去查查文献，应该会有的。

84-1270
看d值
3 strongest lines :2.64    4.97    1.94
对称性：H

我只需要2倍角度数的出峰，不要强度都可以，在20~80度之间

PDF#84-1266: QM=Calculated; d=Calculated; I=Calculated
Calcium Hydroxide
Ca ( O H )2       
Radiation=CuKa1        Lambda=1.54060        Filter=
Calibration=        d-Cutoff=17.7        I/Ic(RIR)=3.69
Ref= Calculated from ICSD using POWD-12++ (1997)

Hexagonal - Single Crystal,  P-3m1 (164)        Z=1        mp=
Cell=3.5993x4.9367        Pearson=hP5 (?)
Density(c)=2.221        Density(m)=2.39A        Mwt=74.09        Vol=55.39        F(18)=346.0(.0027,19)
Ref= Chaix-Pluchery, O., Pannetier, J., Bouillot, J., Niepce, J.C.
J. Solid State Chem., 67 225 (1987)
Strong Line: 2.64/X 4.94/7 1.94/4 1.80/3 3.12/2 1.69/1 1.46/1 1.49/1 1.32/1 1.15/1
FIZ=202223: ATF REM      TEM 110 C.
See PDF 01-084-1271.
Structural prereactional transformations in Ca (O H)2

d(A)     I(f)   I(v)  h  k  l  n^2  2-Theta   Theta  1/(2d)   2pi/d  
4.936   71.8   38.3  0  0  1        17.953   8.977  0.1013  1.2728
3.117   18.0   15.2  1  0  0        28.614  14.307  0.1604  2.0157
2.635  100.0  100.0  0  1  1        33.986  16.993  0.1897  2.3839
2.468    0.8    0.9  0  0  2        36.367  18.184  0.2026  2.5455
1.935   42.2   57.6  0  1  2        46.914  23.457  0.2584  3.2470
1.799   27.2   39.8  1  1  0        50.683  25.342  0.2778  3.4913
1.690   14.9   23.2  1  1  1        54.203  27.102  0.2957  3.7161
1.645    1.3    2.1  0  0  3        55.821  27.911  0.3038  3.8182
1.558    2.2    3.7  2  0  0        59.238  29.619  0.3208  4.0315
1.486   10.9   19.3  2  0  1        62.434  31.217  0.3364  4.2276
1.455   11.8   21.4  1  1  2        63.919  31.959  0.3436  4.3177
1.455   11.8   21.4  1  0  3        63.919  31.959  0.3436  4.3177
1.317    8.6   17.2  2  0  2        71.536  35.768  0.3794  4.7678
1.234    1.6    3.4  0  0  4        77.236  38.618  0.4051  5.0910
1.214    2.5    5.4  1  1  3        78.733  39.366  0.4117  5.1738
1.178    1.6    3.6  2  1  0        81.658  40.829  0.4244  5.3331
1.147    2.5    5.7  1  0  4        84.330  42.165  0.4357  5.4755
1.146    7.6   17.5  1  2  1        84.469  42.234  0.4363  5.4829
1.131    4.0    9.3  0  2  3        85.800  42.900  0.4419  5.5526，