[求助] 文章大修,让补充实验 已有3人参与

Dear***,
  I have now received the comments from the Reviewers of your paper. You will see that they found the work interesting but they have identified a number of concerns that they feel must be addressed before the paper could be published. If you are prepared to undertake the work required, I would be pleased to reconsider my decision.  If you decide to revise the work, please submit a list of changes or a rebuttal against each point raised by the reviewers when you submit the revised manuscript. Please note that if I do not receive your revised manuscript within the next 60 days, the manuscript will be considered withdrawn.
文章审了四个月,只有一个审稿人意见,共给了7条意见,其中两条不知道该怎么回复:
1.有一篇参考文献对我从事的研究进行了理论计算,我认为理论模型有很多简化,结果会有很大的误差,所以我进行了实验研究。评审人让我将实验结果与该参考文献的理论计算进行对比分析。但问题是理论计算采用的一些参数,实验难以测定,结果很难放到一起对比,该怎么回复呢?
2.评审让我对实验中采用的样品进行电镜扫描,对比样品结构异同点。但该样品的制备只能在冬天进行,而且其结构与温度有关,重新制备样品需要大概3到四个月的时间,所以该怎么办呢?
哪位同仁有相关经验,帮帮忙啊。
回复此楼

» 猜你喜欢

» 本主题相关价值贴推荐,对您同样有帮助:

已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

Hsienming

铜虫 (正式写手)

【答案】应助回帖

★ ★ ★
感谢参与,应助指数 +1
smilemoon: 金币+3, ★★★很有帮助 2014-10-01 07:13:08
可以不补充,但要说明理由!比如仅做一个对比结果!说明自己的优点

[ 发自手机版 http://muchong.com/3g ]
4楼2014-10-01 06:28:56
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
查看全部 5 个回答

jiabinlang

新虫 (正式写手)

【答案】应助回帖

★ ★
感谢参与,应助指数 +1
smilemoon: 金币+2 2014-09-30 21:08:56
如果可能办到的话就补实验啊。如果办不到就老实跟审稿人说咯。
2楼2014-09-30 20:57:16
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

smilemoon

至尊木虫 (知名作家)

看来只能好好解释一下了,希望不会被据。
3楼2014-10-01 06:24:24
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

wyliu_as

铁杆木虫 (著名写手)

【答案】应助回帖

感谢参与,应助指数 +1
如果你试验和理论计算的参数设置不一致,你是怎么确定理论计算有很大的误差的呢。不同方法获得结果不能比较吧?
如果补充试验是可以操作的,直接告诉编辑,编辑会同意的,时间上不是聚不聚高的决定因素吧。
请大家去我的版面看看,正在收集开源期刊,http://emuch.net/bbs/myf.php?ffid=282
5楼2014-10-01 11:52:20
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
最具人气热帖推荐 [查看全部] 作者 回/看 最后发表
[考研] 301求调剂 +5 149. 2026-04-10 5/250 2026-04-10 15:45 by 柴小白
[考研] 314求调剂 +23 wakeluofu 2026-04-09 24/1200 2026-04-10 15:31 by MOF_Catal
[考研] 311求调剂 +11 xyp想读书 2026-04-10 12/600 2026-04-10 15:15 by solbeg
[考研] 材料调剂 +5 hzhahg 2026-04-06 5/250 2026-04-10 10:10 by may_新宇
[考研] 085601初试330分找调剂 +10 流心奶黄包l 2026-04-09 10/500 2026-04-10 08:14 by Sammy2
[考研] 297求调剂 +27 GENJIOW 2026-04-07 30/1500 2026-04-09 23:20 by wolf97
[考研] 材料工程调剂 +12 小刘同学吖吖 2026-04-06 13/650 2026-04-09 17:07 by luoyongfeng
[考研] 考研调剂 +13 冰冰,,, 2026-04-07 13/650 2026-04-09 17:01 by Lilly_Li
[硕博家园] 新一代电子信息294求调剂 不挑学校 +5 Ytyt11 2026-04-09 6/300 2026-04-09 14:40 by Ytyt11
[考研] 085600,321分求调剂 +19 大馋小子 2026-04-04 20/1000 2026-04-09 14:12 by Delta2012
[考研] 311求调剂 +6 surte 2026-04-08 13/650 2026-04-09 14:00 by surte
[考研] 070300化学279求调剂 +17 哈哈哈^_^ 2026-04-08 18/900 2026-04-09 10:49 by 三七七想上岸
[考研] 277、学硕,求调剂 数一104, +11 瓶子PZ 2026-04-07 12/600 2026-04-07 23:30 by 一只好果子?
[考研] 一志愿北交大材料工程总分358求调剂 +10 cs0106 2026-04-05 12/600 2026-04-06 19:41 by 无际的草原
[考研] 材料调剂 +5 小刘同学吖吖 2026-04-06 5/250 2026-04-06 18:34 by sherry_1901
[考研] 307求调剂 +3 所念及所望 2026-04-06 3/150 2026-04-06 17:30 by 土木硕士招生
[考研] 求调剂到材料 +5 程9915 2026-04-06 5/250 2026-04-06 15:21 by yulian1987
[考研] 求调剂 +10 chenxrlkx 2026-04-05 10/500 2026-04-06 11:31 by 猪会飞
[考研] 一志愿9材料学硕297已过六级求调剂推荐 +11 adaie 2026-04-04 12/600 2026-04-05 19:04 by 蓝云思雨
[考研] 一志愿北交大材料工程总分358求调剂 +6 cs0106 2026-04-05 6/300 2026-04-05 16:34 by imissbao
信息提示
请填处理意见