[求助] 文章大修,让补充实验 已有3人参与

Dear***,
  I have now received the comments from the Reviewers of your paper. You will see that they found the work interesting but they have identified a number of concerns that they feel must be addressed before the paper could be published. If you are prepared to undertake the work required, I would be pleased to reconsider my decision.  If you decide to revise the work, please submit a list of changes or a rebuttal against each point raised by the reviewers when you submit the revised manuscript. Please note that if I do not receive your revised manuscript within the next 60 days, the manuscript will be considered withdrawn.
文章审了四个月,只有一个审稿人意见,共给了7条意见,其中两条不知道该怎么回复:
1.有一篇参考文献对我从事的研究进行了理论计算,我认为理论模型有很多简化,结果会有很大的误差,所以我进行了实验研究。评审人让我将实验结果与该参考文献的理论计算进行对比分析。但问题是理论计算采用的一些参数,实验难以测定,结果很难放到一起对比,该怎么回复呢?
2.评审让我对实验中采用的样品进行电镜扫描,对比样品结构异同点。但该样品的制备只能在冬天进行,而且其结构与温度有关,重新制备样品需要大概3到四个月的时间,所以该怎么办呢?
哪位同仁有相关经验,帮帮忙啊。
回复此楼

» 猜你喜欢

» 本主题相关价值贴推荐,对您同样有帮助:

已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

jiabinlang

新虫 (正式写手)

【答案】应助回帖

★ ★
感谢参与,应助指数 +1
smilemoon: 金币+2 2014-09-30 21:08:56
如果可能办到的话就补实验啊。如果办不到就老实跟审稿人说咯。
2楼2014-09-30 20:57:16
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

smilemoon

至尊木虫 (知名作家)

看来只能好好解释一下了,希望不会被据。
3楼2014-10-01 06:24:24
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

Hsienming

铜虫 (正式写手)

【答案】应助回帖

★ ★ ★
感谢参与,应助指数 +1
smilemoon: 金币+3, ★★★很有帮助 2014-10-01 07:13:08
可以不补充,但要说明理由!比如仅做一个对比结果!说明自己的优点

[ 发自手机版 http://muchong.com/3g ]
4楼2014-10-01 06:28:56
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

wyliu_as

铁杆木虫 (著名写手)

【答案】应助回帖

感谢参与,应助指数 +1
如果你试验和理论计算的参数设置不一致,你是怎么确定理论计算有很大的误差的呢。不同方法获得结果不能比较吧?
如果补充试验是可以操作的,直接告诉编辑,编辑会同意的,时间上不是聚不聚高的决定因素吧。
请大家去我的版面看看,正在收集开源期刊,http://emuch.net/bbs/myf.php?ffid=282
5楼2014-10-01 11:52:20
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
相关版块跳转 我要订阅楼主 smilemoon 的主题更新
最具人气热帖推荐 [查看全部] 作者 回/看 最后发表
[考研] 一志愿重庆大学085700资源与环境专硕,总分308求调剂 +3 墨墨漠 2026-03-18 3/150 2026-03-21 00:39 by JourneyLucky
[考研] 材料专业求调剂 +6 hanamiko 2026-03-18 6/300 2026-03-21 00:24 by JourneyLucky
[考研] 南昌大学材料专硕311分求调剂 +5 77chaselx 2026-03-20 5/250 2026-03-20 23:42 by lovewei0727
[考研] 330求调剂 +4 小材化本科 2026-03-18 4/200 2026-03-20 23:13 by JourneyLucky
[考研] 一志愿南京理工大学085701资源与环境302分求调剂 +4 葵梓卫队 2026-03-18 6/300 2026-03-20 23:02 by JourneyLucky
[考研] 一志愿武理材料工程348求调剂 +3  ̄^ ̄゜汗 2026-03-19 4/200 2026-03-20 21:01 by zhukairuo
[考研] 一志愿 南京航空航天大学大学 ,080500材料科学与工程学硕 +5 @taotao 2026-03-20 5/250 2026-03-20 20:16 by JourneyLucky
[考研] 353求调剂 +3 拉钩不许变 2026-03-20 3/150 2026-03-20 19:56 by JourneyLucky
[考研] 环境工程调剂 +9 大可digkids 2026-03-16 9/450 2026-03-20 17:38 by 醉在风里
[考研] 286分人工智能专业请求调剂愿意跨考! +3 lemonzzn 2026-03-17 4/200 2026-03-20 11:04 by lemonzzn
[考博] 申博26年 +3 八6八68 2026-03-19 3/150 2026-03-19 19:43 by nxgogo
[考研] 288求调剂,一志愿华南理工大学071005 +5 ioodiiij 2026-03-17 5/250 2026-03-19 18:22 by zcl123
[考研] 0703化学调剂 +5 pupcoco 2026-03-17 8/400 2026-03-19 13:58 by houyaoxu
[考研] 0703化学 305求调剂 +4 FY_yy 2026-03-14 4/200 2026-03-19 05:54 by anny19840123
[考研] 收复试调剂生 +4 雨后秋荷 2026-03-18 4/200 2026-03-18 14:16 by elevennnne
[考研] 0703化学调剂 +3 妮妮ninicgb 2026-03-17 3/150 2026-03-18 10:29 by macy2011
[考研] 301求调剂 +9 yy要上岸呀 2026-03-17 9/450 2026-03-18 08:58 by 无际的草原
[考研] 考研化学学硕调剂,一志愿985 +4 张vvvv 2026-03-15 6/300 2026-03-17 17:15 by ruiyingmiao
[考研] 308求调剂 +4 是Lupa啊 2026-03-16 4/200 2026-03-17 17:12 by ruiyingmiao
[考研] 080500,材料学硕302分求调剂学校 +4 初识可乐 2026-03-14 5/250 2026-03-14 21:08 by peike
信息提示
请填处理意见