[求助] 回答编辑的问题，是小角晶界引起晶格常数偏离理想数值吗？

我们做多晶粉末，随着焙烧温度提高，微晶尺寸增加，晶格常数也趋近理想晶格常数。我们认为是由于粉末颗粒内微晶的无序晶格排列减少造成的，但现在编辑问我们是那种缺陷造成晶格常熟变大！并提出以下几个问题：
“The lattice parameter in Table 1 decreases toward the ideal lattice parameter of **. This may be related to the more and more orderly lattice structure in crystallite/nanoparticle. As the calcination temperature increased, the wrong lattice arrangement in individual crystallite may be reduced so as to optimize the crystal orientation to the same orientation."
This needs to be made clear (i) what lattice defects are thought to increase the lattice parameter (vacancies, dislocations and grain boundaries are not thought to do this), (ii) why the orientation of the crystallite is relevant, and (iii) whether the orientation becomes the same by grain growth or some other mechanism.
请问我该怎么回答这三个问题？真是头疼啊，
微晶内的晶格缺陷主要是点缺陷，线缺陷，面缺陷，体缺陷，现在编辑认为空位和位错不是原因，而我们的粉体没有杂相这些体缺陷。我讨论了下，认为主要是小尺寸微晶融合成大尺寸微晶，形成的小角晶界造成的；因为小角晶界处存在角度偏差，角度弧向处的晶格等于被拉宽。不知道这个对不对，还有 ”小角晶界“的专业英语术语是什么？特此请教各位高人!

回复此楼