[求助]
关于Fe3O4纳米微粒表面巯基或氨基改性的最佳合成方法
|
|
最近想对Fe3O4纳米颗粒进行巯基改性，使用的是MPS，反应条件如下：Modification of MCNCs with MPS was achieved by adding 80 mL of ethanol, 10 mL of deionized water, 1.5 mL of NH3ּH2O, and 0.3 g of MPS into the above ethanol suspension and ultrasounding the mixture for 24 h at 60℃. 但是感觉没接上去，不知道这方法有没不合理之处？另外想请那大看看以下两种方法怎么样？ 1、Fe3O4 纳米颗粒加入100 mL乙醇水溶液中(50%)，用冰醋酸调节pH至4，室温下超声分散1h，加入1 mL硅烷化试剂MPS，N2保护，60℃下反应10 h。 2、Fe3O4 nanoparticles were first dispersed in 20mL deionized-distilled water. Then, the 1 mL of 2.5 mg/mL Fe3O4 nanoparticles solution was dispersed in 5 mL ethanol and sonicated under water bath for 8 h. Meanwhile, 0.3 mL of MPS was added into the 5 mL of ethanol and 0.4 mL of 25% HAc to hydrolyse and condense by sonicating in an ice bath for 30 min. Subsequently, the hydrolysed and condensed MPS (5.3 mL) was added into thus obtained Fe3O4 nanoparticles solution (5.6 mL) by sonicating in an ice bath. 大家有没有更加合理简便的方法能很容易的进行巯基改性呢？要求重复性比较好的 在此先谢过了。 |
回复此楼» 猜你喜欢
求助Fe-TCPP、Zn-TCPP的CIF文件，或者CCDC号
已经有0人回复
-
XPS/?λXPS
已经有0人回复
-
无机化学论文润色/翻译怎么收费?
已经有189人回复
-
河北大学-26年秋季入学化学博士招生
已经有0人回复
-
招收2026年入学博士研究生
已经有10人回复
-
哈尔滨工程大学材化学院国家级青年人才-26年硕士招生/调剂招生
已经有2人回复
» 本主题相关商家推荐: (我也要在这里推广)
找到一些相关的精华帖子，希望有用哦~
Fe3O4的氨基化实验
已经有4人回复
- 溶剂热法合成Fe3O4@PAA问题
已经有5人回复
- 四氧化三铁纳米粒子，与氨水混合，就会聚集，为什么啊？
已经有16人回复
- Fe3O4@SiO2合成中的一些问题
已经有10人回复
- 求教有关Ge Jianping的Fe3O4@PAA合成的问题
已经有23人回复
- Fe3O4@SiO2 表面氨基修饰
已经有11人回复
- Fe3O4表面包覆TiO2包覆不上的问题
已经有22人回复
- 有人会合成Fe3O4纳米粒子/纳米球并功能化上-COOH官能团么
已经有4人回复
- Fe3O4纳米颗粒聚合物凝胶相分散
已经有15人回复
- 多元醇法制备四氧化三铁的干燥过程~
已经有13人回复
- 【求助】Fe3O4 纳米粒子的合成
已经有29人回复
点击这里搜索更多相关资源科研从小木虫开始，人人为我，我为人人