[求助] 论文的状态是Revise-mandatory，有经验的虫子帮看看意见! 已有2人参与

向MSE-A投了篇文章，大概10天左右就一审完成了。
然后状态是Revise-mandatory，第一次发论文，心里没什么底!
但看了审稿人的意见，还是觉得还是有戏的，望有经验的虫子们指点啊。
以下是编辑回复和审稿人的意见：

Dear **,

Your manuscript, "**", is being returned to you with a mandatory revision recommendation.  It will be considered for publication in MSE A provided that it is revised in accord with any below comments of the reviewer or any additional comments and or corrections in the "Reviewer Attachments".

If you choose to revise your manuscript it will be due into the Editorial Office by the Jun 29, 2014.  Please note that this is a strict deadline.  Any papers outstanding in the system after this deadline has expired will be withdrawn unless you have contacted the Editorial Office regarding your revised manuscript.

Please submit your revised paper files as well as the "Detailed Responses to the reviewer comments" file, which incorporates all the reviewer comments and your detailed responses to such, at: http://ees.elsevier.com/msea/
Your username is: ******
If you need to retrieve password details, please go to: http://ees.elsevier.com/msea/automail_query.asp

NOTE: Upon submitting your revised manuscript, please upload the source files for your article. For additional details regarding acceptable file formats, please refer to the Guide for Authors at: http://www.elsevier.com/journals ... 3/guide-for-authors

When submitting your revised paper, we ask that you include the following items:

Response to Reviewers (mandatory)

This should be a separate file labeled "Response to Reviewers" that carefully addresses, point-by-point, the issues raised in the comments appended below. You should also include a suitable rebuttal to any specific request for change that you have not made. Mention the page, paragraph, and line number of any revisions that are made.

Manuscript and Figure Source Files (mandatory)

We cannot accommodate PDF manuscript files for production purposes. We also ask that when submitting your revision you follow the journal formatting guidelines.  Figures and tables may be embedded within the source file for the submission as long as they are of sufficient resolution for Production. Refer to the Guide for Authors for additional information.
http://www.elsevier.com/journals ... 3/guide-for-authors

When submitting your revised paper, please ensure that the item uploaded as "manuscript" is a clean file which incorporates all the revisions/changes and this should be the final version of the main manuscript text. Please do not include the previous (old) version of your manuscript.

Please ensure that the item uploaded as the "marked up manuscript" is the revised file which contains all the revisions/changes made in highlighted font so that one can easily view the revisions/changes made to your revision.

Click on [Author Login]
On your Main Menu page is a folder entitled "Submissions Needing Revision". You will find your submission record there. Click on 'View Reviewer Attachments' (if present) to access any files uploaded by the reviewers.

Kindly use the above manuscript reference number with all correspondence concerning this paper.

Please note that this journal offers a new, free service called AudioSlides: brief, webcast-style presentations that are shown next to published articles on ScienceDirect (see also http://www.elsevier.com/audioslides). If your paper is accepted for publication, you will automatically receive an invitation to create an AudioSlides presentation.

Yours sincerely,

E.J. Lavernia
Editor
Materials Science & Engineering A

Reviewers' comments:

Reviewer #1:
1.    In page 4 line 24 you write "the eutectic phases have a bad bonding with <alpha>-Mg matrix". What do you mean by "bad bonding".
2.    In Fig. 3. (b) Excuse me but I cannot see the interface and eutectic phase near the white arrows.
3.    Please give details of cooling mod after solid - solution treatment (Fig.1. (b)). This information is not presented in the experimental procedures.
4.    In Page 5 line 9 you write "the eutectic phases near the original grain boundaries are dissolved".  What do you mean by "original grain boundaries".