[求助] 提供吸附数据，求指教吸附量为什么那么小

我的配合物是α-Po的结构，孔洞率40%,我用软件测到孔有13.5埃*7.5埃，但是做77k的氮气吸附，吸附量很小。

Surface Area

Single point surface area at p/p° = 0.295106236: 20.4684 m²/g

BET Surface Area: 20.8663 m²/g

BJH Adsorption cumulative surface area of pores
between 1.7000 nm and 300.0000 nm width: 20.986 m²/g

BJH Desorption cumulative surface area of pores
between 1.7000 nm and 300.0000 nm width: 22.9013 m²/g

Pore Volume
Single point adsorption total pore volume of pores
less than 234.3252 nm width at p/p° = 0.991688608: 0.053613 cm³/g
BJH Adsorption cumulative volume of pores
between 1.7000 nm and 300.0000 nm width: 0.053410 cm³/g

BJH Desorption cumulative volume of pores
between 1.7000 nm and 300.0000 nm width: 0.053363 cm³/g
Pore Size
Adsorption average pore width (4V/A by BET): 10.27744 nm
BJH Adsorption average pore width (4V/A): 10.1802 nm
BJH Desorption average pore width (4V/A): 9.3205 nm
Nanoparticle Size:
Average Particle Size 287.5456 nm

BJH孔径分析.jpg

77k氮气吸附解吸.jpg

回复此楼

» 猜你喜欢

1楼2013-06-15 22:45:18

已阅回复此楼关注TA 给TA发消息送TA红花 TA的回帖

上官小仙

木虫 (著名写手)

前世今生

应助: 291 (大学生)
贵宾: 0.038
金币: 4190.1
散金: 2000
红花: 94
帖子: 1334
在线: 187.1小时
虫号: 1730712
注册: 2012-04-01
性别: GG
专业: 电机与电器

【答案】应助回帖

★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
ming142007: 金币+45, ★有帮助, 10 2013-06-19 16:34:25

从你说的那两种孔及孔隙率数据来看，材料应该是微孔材料。既然是微孔结构的孔材料，显然140度处理是不行的，一般要求处理温度不低于180度，最好能到300度才可以使得游离在20A以下的孔内的水汽分子或者杂质气体分子处理掉，处理的时候也要以防发生水热反应。加热可设成梯度加热法。就是不知道300度这么高温度，你的材料能否抗的住