[求助] 求助关于量子点的问题

请问各位高手，有哪一种量子点是在500激发，发射峰在600+的位置的
回复此楼

» 收录本帖的淘帖专辑推荐

Fluorescent Nanomaterials

» 猜你喜欢

» 本主题相关价值贴推荐，对您同样有帮助:
1楼 2012-11-15 19:29:55
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

sally208

专家顾问 (著名写手)

【答案】应助回帖

★ ★ ★ ★ ★ ★ ★ ★ ★ ★
感谢参与，应助指数 +1
3006213050: 金币+10, ★★★很有帮助 2012-11-16 09:10:40
Since semiconductor QDs possess a wide excitation range, thus as soon as you can have QD with emission above 600 nm, they can serve your purpose '量子点是在500激发，发射峰在600+的位置'.
So you have many choices, such as CdTe, CdSe QDs, you just need to control their core size. Few examples in the literature: http://pubs.rsc.org/en/Content/ArticleLanding/2012/NR/c2nr31809a ; http://pubs.rsc.org/en/Content/ArticleLanding/2011/NR/c1nr10933b ; http://pubs.rsc.org/en/Content/ArticleLanding/2011/NR/c1nr10218d ...

Commercially available Qds from Invitrogen: http://www.invitrogen.com/search ... p;resultsPerPage=15
赞一下(2人) 回复此楼
2楼2012-11-16 00:51:33
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

星汉纳米技术

金虫 (小有名气)

【答案】应助回帖

★ ★ ★ ★ ★
感谢参与，应助指数 +1
3006213050: 金币+5, ★★★很有帮助 2012-11-16 09:10:46
量子点的激发光谱很宽，只要发射是在600nm就可以了。可用CdSe/ZnS
赞一下 回复此楼
3楼2012-11-16 08:48:34
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

3006213050

铁虫 (小有名气)
引用回帖:
2楼: Originally posted by sally208 at 2012-11-16 00:51:33
Since semiconductor QDs possess a wide excitation range, thus as soon as you can have QD with emission above 600 nm, they can serve your purpose '量子点是在500激发，发射峰在600+的位置'.
So you have  ...

Thank you for your useful reference. As we know, the emission of QDs can be near- infrared. However, the excitiation range usually was 400-480 nm. such as your ref.2. Making the 500 nm excitaion was a big problem for me. I wish you can give me some advices.
                                                              Sincerely yours.
赞一下 回复此楼
4楼2012-11-16 09:06:51
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

sally208

专家顾问 (著名写手)
引用回帖:
4楼: Originally posted by 3006213050 at 2012-11-16 02:06:51
Thank you for your useful reference. As we know, the emission of QDs can be near- infrared. However, the excitiation range usually was 400-480 nm. such as your ref.2. Making the 500 nm excitaion was ...

I think it is just a matter of excitation efficiency at different wavelength. It is normal that he more bule the excitation wavelength you choose, the lower brightness will the QDs be. Once you have QDs with large quantum yield (e.g., QY > 20%), I do not think it can be a big issue for your experiment, even in single particle imaging experiment with the common lasers, 488 nm or even 532 nm.
赞一下 回复此楼
5楼2012-11-16 15:21:40
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

sally208

专家顾问 (著名写手)
引用回帖:
5楼: Originally posted by sally208 at 2012-11-16 08:21:40
I think it is just a matter of excitation efficiency at different wavelength. It is normal that he more bule the excitation wavelength you choose, the lower brightness will the QDs be. Once you have ...

a mistake in above reply:
... the more blue the excitation wavelength you chose, the higher brightness will the QDs be ...
赞一下 回复此楼
6楼2012-11-16 18:25:24
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

3006213050

铁虫 (小有名气)
引用回帖:
6楼: Originally posted by sally208 at 2012-11-16 18:25:24
a mistake in above reply:
... the more blue the excitation wavelength you chose, the higher brightness will the QDs be ......

Thank you for your attention
赞一下 回复此楼
7楼2012-11-19 18:25:59
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
相关版块跳转 我要订阅楼主 3006213050 的主题更新
71/1返回列表
普通表情 龙 兔 虎 猫
最具人气热帖推荐 [查看全部] 作者 回/看 最后发表
[考研] 一志愿华中农业071010，320求调剂 +5 困困困困坤坤 2026-04-14 6/300 2026-04-14 23:54 by Xurambo2014
[考研] 通信工程求调剂！！！ +4 zlb770521 2026-04-14 4/200 2026-04-14 18:19 by lbsjt
[考研] 08工学 309分求调剂 +12 Yin DY 2026-04-08 12/600 2026-04-14 17:49 by lhj2009
[考研] 367求调剂 +11 hffQAQ 2026-04-09 11/550 2026-04-14 17:48 by lhj2009
[考研] 一志愿西南大学生物学学硕344 求生物学相关调剂/生物与医药 +8 超人不会飞@ 2026-04-08 8/400 2026-04-14 16:06 by zs92450
[考研] 考研求调剂 +6 ban班小七 2026-04-11 6/300 2026-04-14 14:06 by 哆啦A梦只是个梦
[考研] 085404 298分求调剂 +11 呼啦呼啦呼呼呼 2026-04-10 12/600 2026-04-14 08:38 by wfj257
[考研] 344 材料专业 求调剂211 无地域要求 +8 hualkop 2026-04-11 8/400 2026-04-12 22:24 by fqwang
[考研] 0831生医工第一轮调剂失败求助 +12 小熊睿睿_s 2026-04-11 16/800 2026-04-12 16:28 by 钰璞
[考研] 291求调剂 +11 关忆北. 2026-04-09 12/600 2026-04-12 10:32 by 逆水乘风
[考研] 283求调剂 086004考英二数二 +17 那个噜子 2026-04-10 18/900 2026-04-11 16:27 by 明月此时有
[考研] 087100初试311求调剂 +4 任雅琴 2026-04-09 4/200 2026-04-11 10:33 by zhq0425
[考研] 0854调剂 +8 950824he@ 2026-04-09 8/400 2026-04-11 10:11 by zhq0425
[考研] 284求调剂 +12 archer.. 2026-04-10 13/650 2026-04-11 08:44 by zhq0425
[考研] 调剂 化学 307 +21 73372112 2026-04-09 23/1150 2026-04-10 23:53 by wj165256
[考研] 一志愿北理工298英一数二已上岸，感谢各位老师 +14 Reframe 2026-04-10 16/800 2026-04-10 23:07 by caotw2020
[考研] 计算机类求调剂，22408-274分 +7 上岸de小虫 2026-04-09 8/400 2026-04-10 19:56 by fxue1114
[考研] 一志愿京区985，085401电子信息，本科电子信息 +3 阳光开朗的男孩 2026-04-10 3/150 2026-04-10 16:29 by sophia_93
[考研] 一志愿中南大学物理学，英一66，求调剂 +4 长烟旖旎 2026-04-08 5/250 2026-04-10 10:31 by 颖果儿
[考研] 286求调剂 +19 Faune 2026-04-08 20/1000 2026-04-09 08:36 by 哦哦123
信息提示
关闭
请填处理意见
关闭