2.1. Synthesis of cobalt ferriteCoFe2O4 (sample CFO) was synthesized by chemical coprecipitationby the following procedure. A 0.2 M solutionwas prepared by dissolving Co(NO3)26H2O (A.C.S.reagent, Aldrich) and Fe(NO3)39H2O (puriss, Fluka) in deionized water. The precipitating agent was a 5 M NaOH(reagent grade, Aldrich) solution with 100% molar excess.
Both solutions were heated separately to 65 C and thenmixed under constant stirring. The temperature was raised to 80 C for 20 min, to completely crystallize the spinel phase. The precipitate was centrifuged and thoroughly washed with distilled water. The cobalt ferrite was kept in a water suspension. One small portion was dried at 80 C for characterization.
2.2. Preparation of a ferrofluid
The cobalt ferrite/water suspension was heated to 80 C under gentle stirring. Oleic acid (reagent grade, Sigma– Aldrich) was added to the suspension at 30 wt.% with respect to the cobalt ferrite. The temperature was raised to 90 C for 30 min and then cooled to 60 C. Octane (reagent grade, Sigma–Aldrich) was added and the mixture was stirred for another 30 min. During this process, the
nanoparticles were transferred from the aqueous phase to the organic phase, thus forming the ferrofluid. Prior to its collection, the ferrofluid was washed with distilled water in a separatory funnel to remove the non-modified particles.
A gravimetric study of a 2.5 g aliquot was carried out to determine the content of inorganic material in the ferrofluid by weight difference before and after calcination
at 700 C. A sample of the surface-modified ferrite was reserved before the addition of octane to determine the amount of oleic acid that reacted with the particles. The sample was dried at 80 C before performing a thermogravimetric analysis on a TGA Q500 by TA Instruments, from room temperature to 700 C at 5 min1.
2.3. Synthesis of cobalt ferrite–barium titanate core–shelltype
nanostructures Core–shell-like nanostructures of CoFe2O4–BaTiO3 were synthesized by the sol–gel technique. Ba(C2H3O2)2 (A.C.S. reagent, Sigma–Aldrich) was mixed with titanium (IV) n-butoxide (reagent grade, Sigma–Aldrich), stearic acid (95%, Sigma–Aldrich) and glacial acetic acid (Aldrich)
at 90 C to form a sol. The ferrofluid was added to the sol at an adequate amount so that the final nanostructures have a content of 20, 30, 40, 50 and 60 wt.% of cobalt ferrite with respect to the barium titanate, namely samples Co20, Co30, Co40, Co50 and Co60, respectively. Anhydrous 2-methoxyethanol (Aldrich) was added to promote the gel formation. The obtained gels were dried overnight
at 80 C and sintered at 700 C for 2 h under the following conditions: (a) heating rate of 1.8 C min1 from room temperature to 350 C; (b) heating rate of 1.5 C min1 from 350 C to 700 C and (c) cooling rate of 4 C min1
from 700 C to room temperature, to avoid cracking of the barium titanate, which is the shell in the nanostructures and is expected to be subjected to high stresses. One additional sample without ferrofluid was also prepared as a reference
(sample BTO). All samples were washed with a 0.1 M acetic acid solution to dissolve impurities such as barium carbonate [18]. We note that if the stearic acid, glacial acetic acid and 2-methoxyethanol were omitted from the preparation, the resulting material consisted of a simple mixture of individual cobalt ferrite and barium titanate nanoparticles.

» 猜你喜欢

» 抢金币啦!回帖就可以得到:

查看全部散金贴

已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

lidan0123

银虫 (正式写手)


引用回帖:
Originally posted by 8814402 at 2011-02-12 21:34:37:
如果你觉得翻译也就那么回事,自个弄去,别在这剽窃别人的劳动

你这人会不会说话啊,我只是看不懂,问一下不行啊?你看见我剽窃啦?
5楼2011-02-13 07:57:57
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
查看全部 8 个回答
你给50金币也不见得有人译啊
2楼2011-02-12 21:33:29
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
如果你觉得翻译也就那么回事,自个弄去,别在这剽窃别人的劳动
3楼2011-02-12 21:34:37
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

jiangxue82

木虫 (著名写手)


有点多~~楼主给力啊!
4楼2011-02-12 21:53:23
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
普通表情 高级回复 (可上传附件)
最具人气热帖推荐 [查看全部] 作者 回/看 最后发表
[考研] 生物学调剂招人!!! +3 山海天岚 2026-03-17 4/200 2026-03-19 21:34 by 怎么释怀
[考研] 一志愿南京理工大学085701资源与环境302分求调剂 +3 葵梓卫队 2026-03-18 5/250 2026-03-19 19:35 by 给你你注意休息
[考研] 321求调剂 +8 何润采123 2026-03-18 10/500 2026-03-19 16:46 by 何润采123
[考研] 266求调剂 +5 阳阳哇塞 2026-03-14 10/500 2026-03-19 15:08 by 阳阳哇塞
[考研] 317求调剂 +3 申子申申 2026-03-19 6/300 2026-03-19 14:16 by 申子申申
[考研] 一志愿南昌大学,327分,材料与化工085600 +3 Ncdx123456 2026-03-19 3/150 2026-03-19 13:18 by houyaoxu
[考研] 0817调剂 +3 没有答案_ 2026-03-14 3/150 2026-03-19 09:51 by Xu de nuo
[考研] 本科郑州大学物理学院,一志愿华科070200学硕,346求调剂 +4 我不是一根葱 2026-03-18 4/200 2026-03-19 09:11 by 浮云166
[考研] 材料专硕英一数二306 +5 z1z2z3879 2026-03-18 5/250 2026-03-19 07:43 by BruceLiu320
[考研] 354求调剂 +4 Tyoumou 2026-03-18 7/350 2026-03-18 21:45 by Tyoumou
[考研] 328求调剂,英语六级551,有科研经历 +3 生物工程调剂 2026-03-17 7/350 2026-03-18 20:41 by Wangjingyue
[考研] 0854可跨调剂,一作一项核心论文五项专利,省、国级证书40+数一英一287 +8 小李0854 2026-03-16 8/400 2026-03-18 14:35 by 搏击518
[考研] 0703化学调剂 +3 妮妮ninicgb 2026-03-17 3/150 2026-03-18 10:29 by macy2011
[考研] 268求调剂 +8 一定有学上- 2026-03-14 9/450 2026-03-17 17:47 by laoshidan
[考研] 26考研求调剂 +6 丶宏Sir 2026-03-13 6/300 2026-03-17 16:13 by 醉在风里
[考研] 一志愿南京大学,080500材料科学与工程,调剂 +4 Jy? 2026-03-16 4/200 2026-03-17 11:02 by gaoqiong
[考研] 302求调剂 +4 小贾同学123 2026-03-15 8/400 2026-03-17 10:33 by 小贾同学123
[考研] 283求调剂 +3 听风就是雨; 2026-03-16 3/150 2026-03-17 07:41 by 热情沙漠
[考研] 0856求调剂 +3 刘梦微 2026-03-15 3/150 2026-03-16 10:00 by houyaoxu
[考研] 22408总分284求调剂 +3 InAspic 2026-03-13 3/150 2026-03-15 11:10 by zhq0425
信息提示
请填处理意见