当W=20时,样品由刺猬状硫化铜微米球组成,微米球表面由大量薄而光滑的纳米片构成,其直径为1微米,而且样品分散均匀,无明显的团聚现象。而当W增加到30、40时,样品的形貌并没有明显的改变,但其直径分别变为2微米、3微米。从实验结果可以看出,随着W值的增大,硫化铜的尺寸有所增加,但不成一定的正比关系。

» 猜你喜欢

» 抢金币啦!回帖就可以得到:

查看全部散金贴

已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
zhigang985(金币+10, 翻译EPI+1): 2011-01-18 10:36:45
When W=20,the sample was composed of CuS microsphere particles,the surface of microsphere particles were formed by a lot of thin and smoothly nanoslices which paradiameter around 1 micron but also the sample dispersed uniformly and there was no coacervation between the particles.When W increased to 30 or 40,there was no significant change about the sample’s morphology, nevertheless,the diameters changed into 2 micron and 3 micron,respectively.The results indicated that with the increasing value of W,the size of CuS increased gently but not indefinitely showed linear relationship.
3楼2011-01-17 20:01:24
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
查看全部 6 个回答

Risingstar

铁杆木虫 (著名写手)


zhigang985(金币+15): 2011-01-18 10:36:52
不如这样吧

When W = 20, the samples consisted of hedgehog-like CuS microspheres, the surface of which was structured with a large number of thin, smooth nano-sheets. The microspheres were 1 micron in diameter, and homogeneously distributed with no obvious aggregation. When W increased to 30 and 40, no significant change in the morphology of the samples was observed, but the diameter shifted to 2 microns and 3 microns, respectively. It can be seen from the experiment results that, the increase in the value of W leads to an increase in the size of CuS, but not necessarily in a certain proportional relationship.

请LZ斟酌!
4楼2011-01-17 23:54:49
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

Risingstar

铁杆木虫 (著名写手)


zhigang985(金币+3): 2011-01-18 10:37:07
引用回帖:
Originally posted by Risingstar at 2011-01-17 23:54:49:
不如这样吧

When W = 20, the samples consisted of hedgehog-like CuS microspheres, the surface of which was structured with a large number of thin, smooth nano-sheets. The microspheres were 1 micr ...

最后一句“有所增加”补上

...the increase in the value of W leads to a slight increase in the size of CuS...
5楼2011-01-17 23:59:54
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

yuanke520

禁虫 (著名写手)

zhigang985(金币+2): 2011-01-18 10:37:00
本帖内容被屏蔽

6楼2011-01-18 00:08:48
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
普通表情 高级回复 (可上传附件)
最具人气热帖推荐 [查看全部] 作者 回/看 最后发表
[考研] 290求调剂 +6 @将就将就看 2026-03-10 11/550 2026-03-17 10:22 by @将就将就看
[考研] 268求调剂 +6 一定有学上- 2026-03-14 7/350 2026-03-17 10:14 by Sammy2
[考研] 211本,11408一志愿中科院277分,曾在中科院自动化所实习 +5 Losir 2026-03-12 6/300 2026-03-17 10:01 by 求调剂zz
[考研] 材料与化工304求B区调剂 +7 邱gl 2026-03-11 8/400 2026-03-17 09:36 by 努力学习赚彩礼
[考研] 08工科 320总分 求调剂 +3 梨花珞晚风 2026-03-17 3/150 2026-03-17 09:04 by 晗晗调剂上岸
[考研] 304求调剂 +7 小熊joy 2026-03-14 7/350 2026-03-17 08:53 by 雾散后相遇lc
[考研] 一志愿,福州大学材料专硕339分求调剂 +3 木子momo青争 2026-03-15 3/150 2026-03-17 07:52 by laoshidan
[考研] 274求调剂 +5 时间点 2026-03-13 5/250 2026-03-17 07:34 by 热情沙漠
[考研] 0854控制工程 359求调剂 可跨专业 +3 626776879 2026-03-14 9/450 2026-03-16 17:42 by 626776879
[考研] 环境工程调剂 +6 大可digkids 2026-03-16 6/300 2026-03-16 17:16 by barlinike
[考研] 283求调剂 +10 小楼。 2026-03-12 14/700 2026-03-16 16:08 by 13811244083
[考研] 0856求调剂 +3 刘梦微 2026-03-15 3/150 2026-03-16 10:00 by houyaoxu
[考研] 311求调剂 +6 冬十三 2026-03-15 6/300 2026-03-16 08:00 by wang_dand
[考研] 327求调剂 +4 Ffff03 2026-03-10 4/200 2026-03-14 00:17 by JourneyLucky
[考研] 复试调剂 +9 Copy267 2026-03-10 9/450 2026-03-13 23:45 by userper
[考研] 材料与化工求调剂一志愿 985 总分 295 +8 dream…… 2026-03-12 8/400 2026-03-13 22:17 by 星空星月
[考研] 295求调剂 +3 小匕仔汁 2026-03-12 3/150 2026-03-13 15:17 by vgtyfty
[考研] 一志愿山大07化学 332分 四六级已过 本科山东双非 求调剂! +3 不想理你 2026-03-12 3/150 2026-03-13 14:18 by JourneyLucky
[考研] 081200-11408-276学硕求调剂 +3 崔wj 2026-03-12 4/200 2026-03-12 19:33 by 求调剂zz
[考博] 26申博求助 +3 跳跃饼干 2026-03-10 4/200 2026-03-10 21:15 by Tntcnn
信息提示
请填处理意见