liuwenyan铁虫 (正式写手)
|
[交流]
【请教】水相法制备微米硅球出现的问题,恳求高手指点迷津
|
|||
|
我想问一下各位高手,有没人重复过文献Yong-Geun Lee, Jae-Hyung Park, Chul Oh, Seong-Geun Oh,* and Young Chai Kim, Preparation of Highly Monodispersed Hybrid Silica Spheres Using a One-Step Sol-Gel Reaction in Aqueous Solution,Langmuir 2007, 23(22):10875-10878中用水相法制备微米硅球的实验. 最近我重复了好几次,都是以失败而告终,郁闷之极. 文献中提到"Each amount of MPTMS (1, 10, and 20 g) was added into 100 g of water under vigorous stirring until the oil (MPTMS) droplets completely disappeared and a transparent solution was obtained.NH4OH (0.1 mL) was added to the mixture solution (pH11), and then the reaction progressed during 12 h at room temperature." 第一步透明溶液我已得到.第二步我有些不明白,PH=11,是怎么回事?透明溶液的pH=4~5,无论我是用氨水还是NaOH调pH值,调到pH=8时,就会有大量沉淀产生,致使搅拌棒无法搅动,反应不得不中止.应该是发生了交联了吧. 第二步加入NH4OH后,反应的搅拌速度最佳是多少? 各位高手,指点一下迷津吧.谢谢! [ Last edited by liuwenyan on 2009-6-15 at 20:52 ] |
回复此楼» 收录本帖的淘帖专辑推荐
 二氧化硅微球制备及表面改性 |
» 猜你喜欢
请问对标matlab的开源软件octave的网站https://octave.org为什么打不开？
已经有1人回复
-
求助两种BiOBr晶体的CIF文件（卡片号为JCPDS 09-0393与JCPDS 01-1004 ）
已经有0人回复
-
金属材料论文润色/翻译怎么收费?
已经有206人回复
-
哈尔滨工程大学材化学院国家级青年人才-26年硕士招生
已经有0人回复
-
求助Fe-TCPP、Zn-TCPP的CIF文件，或者CCDC号
已经有0人回复
-
河北大学-26年秋季入学申请考核制-化学博士1名
已经有0人回复
-
XPS/?λXPS
已经有0人回复
2楼2009-06-15 21:51:10
3楼2009-06-15 21:53:45
liuwenyan
铁虫 (正式写手)
- 应助: 0 (幼儿园)
- 金币: 98.3
- 散金: 28
- 帖子: 316
- 在线: 17.1小时
- 虫号: 425956
- 注册: 2007-07-28
- 性别: MM
- 专业: 环境分析化学
4楼2009-06-16 08:40:16
liuwenyan
铁虫 (正式写手)
- 应助: 0 (幼儿园)
- 金币: 98.3
- 散金: 28
- 帖子: 316
- 在线: 17.1小时
- 虫号: 425956
- 注册: 2007-07-28
- 性别: MM
- 专业: 环境分析化学
5楼2009-06-16 08:44:01