汉译英，求润色，122个字，谢谢。
|
|||
|
在300°C左右，两个样品都出现了模量峰。样品KS的模量峰值要略高于样品LS的模量峰值，而峰温却低于样品LS的峰温。样品KS和LS经过热处理后产生了元素扩散，样品KS和LS的扩散斜率k分别为k1=60.9和k2=45.7，模量峰值分别为E1= 1.6E11和E2 =2.3E11，则单位扩散斜率上的模量峰值可用∆E / k表示。 At about 300 ° C, two samples appeared modulus peaks. Modulus peak value of the sample KS was slightly higher than that of the sample LS, while the peak temperature is lower than the peak temperature of the sample LS. After heat treatment samples KS and LS produced element diffusion, and the diffusion slope k of the sample KS and LS were k1 = 60.9 and k2 = 45.7, respectively corresponding to modulus peak value E1 = 1.6E11 and E2 = 2.3E11. ΔE/k represented the modulus peak on unit diffusion slope. |
回复此楼» 猜你喜欢
依托企业入选了国家启明计划青年人才。有无高校可以引进的。
已经有11人回复
-
依托企业入选了国家启明计划青年人才。有无高校可以引进的。
已经有10人回复
-
同年申请2项不同项目，第1个项目里不写第2个项目的信息，可以吗
已经有9人回复
-
有时候真觉得大城市人没有县城人甚至个体户幸福
已经有11人回复
-
表哥与省会女结婚，父母去帮带孩子被省会女气回家生重病了
已经有7人回复
-
天津大学招2026.09的博士生，欢迎大家推荐交流（博导是本人）
已经有9人回复
-
有院领导为了换新车，用横向课题经费买了俩车
已经有10人回复
-
AI 太可怕了，写基金时，提出想法，直接生成的文字比自己想得深远，还有科学性
已经有6人回复
【答案】应助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
真强必胜: 金币+1, good 2014-07-12 11:33:18
wxqtjw: 金币+10, 翻译EPI+1 2014-07-14 14:49:54
真强必胜: 金币+1, good 2014-07-12 11:33:18
wxqtjw: 金币+10, 翻译EPI+1 2014-07-14 14:49:54
| At about 300 ° C, the modulus peaks of two samples appeared.Modulus peak value of sample KS was slightly higher than sample LS's.But the peak temperature of sample KS is lower than sample LS's.The elements of sample KS and LS have been diffused after heating treatment and the diffusion slope k of the sample KS and LS were k1 = 60.9 and k2 = 45.7,respectively corresponding to modulus peak value were E1 = 1.6E11 and E2 = 2.3E11. ΔE/k represented the modulus peak on unit diffusion slope. |
2楼2014-07-11 15:30:00
【答案】应助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
真强必胜: 金币+1, 多谢 2014-07-12 11:33:36
wxqtjw: 金币+20, ★★★★★最佳答案 2014-07-14 14:50:02
真强必胜: 金币+1, 多谢 2014-07-12 11:33:36
wxqtjw: 金币+20, ★★★★★最佳答案 2014-07-14 14:50:02
|
请参考： At about 300 ° C, modulus peaks have been observed in two samples. The value of modulus peak for sample KS was slightly higher than that for sample LS, whereas the peak temperature of KS is lower than that of the sample LS. After treatment by heating, the element diffusion appeared in KS and LS and the diffusion slope k of KS and LS were k1 = 60.9 and k2 = 45.7 respectively and the corresponding value of modulus peak are E1 = 1.6E11 and E2 = 2.3E11. Therefore ΔE/k represents the modulus peak for unit diffusion slope. |
3楼2014-07-12 02:33:06
love林之海
铁虫 (小有名气)
- 应助: 8 (幼儿园)
- 金币: 106.5
- 散金: 51
- 帖子: 95
- 在线: 43.2小时
- 虫号: 3315678
- 注册: 2014-07-09
- 专业: 生物医用高分子材料
【答案】应助回帖
|
At 300 ° C, two samples appeared modulus peak. Modulus modulus peak peak slightly higher than the sample sample KS LS, and the peak temperature is lower than the peak temperature of sample LS. Samples of KS and LS after heat treatment produced the element diffusion, dispersion slope k samples KS and LS were k1=60.9 and k2=45.7, respectively E1= and 1.6E11 modulus peak of E2 =2.3E11, the unit diffusion modulus peak slope can be used on the delta E / K. [ 发自小木虫客户端 ] |
4楼2014-07-12 21:15:41