[求助] 审稿意见求助

Ball and disc configuration where disc is TiC reinforced alloy, you have seen increased CoF and low wear. If the case is disc on disc both counter parts includes hard TiC particles in alloy, do you think the case will be the same? I think hard TiC particles may generate scratches, cracks and more wear. In this case so scenario may be different. It is not in the exact scope of in this paper, but making a direct conclusion TiC adding reduces the wear may not be correct as a general statement. It will bring a value into paper a short discussing on this by the support of literature.

上面这段是审稿人给的一个审稿意见，查了大量的文献没有发现盘盘接触的模式，另外我认为球盘接触模式，和盘盘接触模式应该是一样的摩擦磨损形式吧！球盘接触面扩大就是盘盘接触吧！！！！请高手指教！！！