[交流] 【求助】急求Cu2o 的pdf卡片!用于做标准图谱的!急求谢谢!!!!! 已有2人参与

求帮忙!!!!!
回复此楼
已阅   关注TA 给TA发消息 送TA红花 TA的回帖

gyliu

铁杆木虫 (职业作家)


小木虫(金币+0.5):给个红包,谢谢回帖交流
PDF#65-3288: QM=Calculated; d=Calculated; I=Calculated
Copper Oxide
Cu2 O       
Radiation=CuKa1        Lambda=1.54060        Filter=
Calibration=        d-Cutoff=        I/Ic(RIR)=8.63
Ref= Calculated from NIST using POWD-12++

Cubic - (Unknown),  Pn-3m (224)        Z=2        mp=
Cell=4.26        Pearson=cP6 (Ag2 O)
Density(c)=6.146        Density(m)=6.090        Mwt=143.09        Vol=77.31        F(20)=999.9(.0003,20)
Ref= M.Neuberger
Z. Kristallogr., Kristallgeom., Kristallphys., Kristallchem., 77 169 (1931)
Strong Line: 2.46/X 2.13/4 1.51/3 1.28/2 0.98/1 0.87/1 0.82/1 3.01/1 0.95/1 1.23/1
NOTE:  N AL4552       3545 IB=Cu,O See PDF 01-077-0199.
d(A)          I(f)        I(v)        h        k        l         n^2        2-Theta        Theta        1/(2d)        2pi/d       
3.0123        5.3        4.3        1        1        0        2        29.632        14.816        0.1660        2.0859       
2.4595        100.0        100.0        1        1        1        3        36.502        18.251        0.2033        2.5546       
2.1300        35.3        40.8        2        0        0        4        42.401        21.201        0.2347        2.9499       
1.7391        1.2        1.7        2        1        1        6        52.579        26.290        0.2875        3.6128       
1.5061        28.6        46.7        2        2        0        8        61.518        30.759        0.3320        4.1717       
1.4200        0.1        0.2        2        2        1        9        65.701        32.851        0.3521        4.4248       
1.3471        0.3        0.5        3        1        0        10        69.751        34.875        0.3712        4.6641       
1.2844        22.2        42.5        3        1        1        11        73.697        36.848        0.3893        4.8918       
1.2298        4.8        9.6        2        2        2        12        77.565        38.783        0.4066        5.1093       
1.1385        0.3        0.6        3        2        1        14        85.150        42.575        0.4392        5.5187       
1.0650        2.9        6.7        4        0        0        16        92.650        46.325        0.4695        5.8997       
1.0332        0.1        0.2        3        2        2        17        96.409        48.205        0.4839        6.0813       
1.0041        0.1        0.2        4        1        1        18        100.196        50.098        0.4980        6.2576       
0.9773        6.7        16.9        3        3        1        19        104.028        52.014        0.5116        6.4291       
0.9526        5.0        12.9        4        2        0        20        107.926        53.963        0.5249        6.5961       
0.9296        0.1        0.3        4        2        1        21        111.912        55.956        0.5379        6.7590       
0.9082        0.1        0.3        3        3        2        22        116.013        58.006        0.5505        6.9180       
0.8696        5.9        16.7        4        2        2        24        124.705        62.352        0.5750        7.2256       
0.8355        0.1        0.3        4        3        1        26        134.437        67.219        0.5985        7.5207       
0.8198        5.9        17.7        5        1        1        27        139.953        69.977        0.6099        7.6639
2楼2011-01-13 09:59:13
已阅   关注TA 给TA发消息 送TA红花 TA的回帖

gyliu

铁杆木虫 (职业作家)


小木虫(金币+0.5):给个红包,谢谢回帖交流
PDF#34-1354: QM=Intermediate; d=(Unknown); I=Film/Visual
Copper Oxide
Cu2 O       
Radiation=MoKa        Lambda=0.710688        Filter=
Calibration=        d-Cutoff=        I/Ic(RIR)=
Ref= Kalliomaki, M. et al.
Phys. Status Solidi, 56 K127 (1979)
Cubic - (Unknown),  Pn-3m (224)        Z=2        mp=
Cell=4.217        Pearson=cP6 (Ag2 O)
Density(c)=6.337        Density(m)=8.80A        Mwt=143.09        Vol=74.99        F(5)=9.3(0.067,8)
Ref= Ibid.

Strong Line: 2.43/X 2.12/X 1.49/8 1.27/5 2.98/3 0.00/1 0.00/1 0.00/1 0.00/1 0.00/1
NOTE:  The X-ray samples were prepared from small crystals of optical quality and were studied in a diamond anvil cell under hydrostatic or quasi-hydrostatic pressure, the pressure was calibrated against a NaCl scale.
Pattern at high pressure, 5.0 GPa.
d(A)          I(f)        I(v)        h        k        l         n^2        2-Theta        Theta        1/(2d)        2pi/d       
2.9780        25.0        17.0        1        1        0        2        29.981        14.990        0.1679        2.1099       
2.4270        100.0        82.0        1        1        1        3        37.009        18.505        0.2060        2.5889       
2.1200        100.0        93.0        2        0        0        4        42.611        21.305        0.2358        2.9638       
1.4860        75.0        100.0        2        2        0        8        62.444        31.222        0.3365        4.2283       
1.2740        50.0        78.0        3        1        1        11        74.402        37.201        0.3925        4.9319
3楼2011-01-13 10:00:27
已阅   关注TA 给TA发消息 送TA红花 TA的回帖

gyliu

铁杆木虫 (职业作家)

PDF#05-0667: QM=Star(+); d=(Unknown); I=Diffractometer
Cuprite, syn
Cu2 +1 O        (Violet red)
Radiation=CuKa1        Lambda=1.5405        Filter=Ni
Calibration=        d-Cutoff=        I/Ic(RIR)=
Ref= Swanson, Fuyat.
Natl. Bur. Stand. (U.S.), Circ. 539, II 23 (1953)
Cubic - Powder Diffraction,  Pn-3m (224)        Z=2        mp=
Cell=4.2696        Pearson=cP6 (Ag2 O)
Density(c)=6.100        Density(m)=8.80A        Mwt=143.09        Vol=77.83        F(13)=56.3(.0115,20)
Ref= Restori, R., Schwarzenbach, D.
Acta Crystallogr., Sec. B: Structural Science, 42 201 (1986)
Strong Line: 2.47/X 2.14/4 1.51/3 1.29/2 3.02/1 1.23/1 0.98/1 0.95/1 0.87/1 0.82/1
NOTE:  Sample prepared at NBS, Gaithersburg, Maryland, USA, by sintering CuCl and Na2 C O2 at ~800 C, then leaching with water and drying.
See ICSD 38233 (PDF 01-077-0199); See ICSD 63281 (PDF 01-078-2076).
Spectroscopic analysis: <1% Ca, Si; <0.1% Al, Mg; <0.01% Ag, B, Ba, Fe, Ti; <0.001% Mn, Pb, Sn.
Pattern taken at 26 C.
Opaque mineral optical data on specimen from Liskeard, Cornwall, England, UK.
Pattern reviewed by Martin, K., McCarthy, G., North Dakota State Univ., Fargo, North Dakota, USA, ICDD Grant-in-Aid (1990).
Agrees well with experimental and calculated patterns.
Additional weak reflection [indicated by brackets] was observed.
d(A)          I(f)        I(v)        h        k        l         n^2        2-Theta        Theta        1/(2d)        2pi/d       
3.0200        9.0        7.0        1        1        0        2        29.554        14.777        0.1656        2.0805       
2.4650        100.0        100.0        1        1        1        3        36.418        18.209        0.2028        2.5490       
2.1350        37.0        43.0        2        0        0        4        42.297        21.149        0.2342        2.9429       
1.7430        1.0        1.0        2        1        1        6        52.454        26.227        0.2869        3.6048       
1.5100        27.0        44.0        2        2        0        8        61.344        30.672        0.3311        4.1611       
1.3502        1.0        2.0        3        1        0        10        69.569        34.785        0.3703        4.6535       
1.2870        17.0        33.0        3        1        1        11        73.526        36.763        0.3885        4.8820       
1.2330        4.0        8.0        2        2        2        12        77.323        38.662        0.4055        5.0959       
1.0674        2.0        5.0        4        0        0        16        92.380        46.190        0.4684        5.8864       
0.9795        4.0        10.0        3        3        1        19        103.701        51.850        0.5105        6.4147       
0.9548        3.0        8.0        4        2        0        20        107.558        53.779        0.5237        6.5806       
0.8715        3.0        8.0        4        2        2        24        124.222        62.111        0.5737        7.2096       
0.8216        3.0        9.0        5        1        1        27        139.284        69.642        0.6086        7.6475
4楼2011-01-13 10:01:26
已阅   关注TA 给TA发消息 送TA红花 TA的回帖

taliayoung

新虫 (初入文坛)

万分感谢!!!
5楼2011-01-13 11:10:07
已阅   关注TA 给TA发消息 送TA红花 TA的回帖
相关版块跳转 我要订阅楼主 taliayoung 的主题更新
最具人气热帖推荐 [查看全部] 作者 回/看 最后发表
[考研] 材料085601调剂 +25 何润采123 2026-04-10 27/1350 2026-04-10 23:17 by Ftglcn90
[考研] 346,工科0854求调剂,专硕 +5 moser233 2026-04-10 6/300 2026-04-10 18:04 by 周邵阳
[考研] 085404 298分求调剂 +10 呼啦呼啦呼呼呼 2026-04-10 11/550 2026-04-10 16:44 by wangy0907
[考研] 085800 能源动力求调剂 +6 阿biu啊啊啊啊啊 2026-04-10 6/300 2026-04-10 15:03 by hemengdong
[考研] 机械还有还有名额吗?太难了 +6 笑笑袁 2026-04-10 6/300 2026-04-10 11:54 by 高维春
[考研] 298求调剂 +8 钉叮咚冬瓜 2026-04-07 10/500 2026-04-10 11:25 by 高维春
[考研] 材料工程302分求调剂 +18 zyx上岸! 2026-04-04 18/900 2026-04-10 10:07 by 314126402
[考研] 求调剂 +15 张zic 2026-04-05 16/800 2026-04-10 08:12 by kangsm
[考研] 一志愿2110,化学学硕310分,本科重点双非求调剂 +18 努力奋斗112 2026-04-08 18/900 2026-04-09 23:28 by wolf97
[考研] 已调剂 +18 柴郡猫_ 2026-04-09 19/950 2026-04-09 22:10 by 柴郡猫_
[考研] 085600材料与化工专硕329 求调剂 +24 额cc 2026-04-06 25/1250 2026-04-09 16:01 by wp06
[考研] 085404,334分,求调剂 +5 sunjie8888 2026-04-08 8/400 2026-04-09 07:26 by sunjie8888
[考研] 二次调剂求老师收留 +3 笑笑袁 2026-04-08 3/150 2026-04-08 23:50 by 醉在风里
[考研] 一志愿南京航空航天大学 材料与化工329分求调剂 +11 Mr. Z 2026-04-05 12/600 2026-04-08 16:15 by luoyongfeng
[考研] 363求调剂 +9 zh096 2026-04-04 9/450 2026-04-07 21:51 by 418490947
[考研] 325 调剂 +6 QQ小虾 2026-04-07 6/300 2026-04-07 15:17 by Ccclqqq
[考研] 081200-11408-276学硕求调剂 +4 崔wj 2026-04-04 5/250 2026-04-05 14:06 by imissbao
[考研] 358求调剂 +7 秋gk 2026-04-04 7/350 2026-04-05 13:29 by huangmoli
[考研] 085602调剂 初试总分335 +12 19123253302 2026-04-04 12/600 2026-04-05 08:08 by 544594351
[考研] 考研调剂 +11 小sun要好运 2026-04-04 11/550 2026-04-05 08:02 by qlm5820
信息提示
请填处理意见