cuoce木虫 (小有名气)
|
[求助]
二氧化硅包覆金棒后离心无法溶解在乙醇中的问题
|
|
|
请教各位，我用二氧化硅包覆金棒，参考的文献的方法是：the CTAB surfactants in the crude GNRs suspension (200 mL) were removed via two cycles of centrifugation/rinsing (12000 rpm, 15 min), and then re-dispersed in 50 mL Milli-Q water. Subsequently, it was transferred into an aqueous solution of CTAB (250 mL, 0.8 mM), and KOH solution (0.1 M) was added to adjust the pH value to ca. 10. After equilibration at 33 °C for 30 min, a solution of TEOS/APTES/ethanol (0.9 mL, 1/0.05/4 vol.) was added into the mixture by three times (0.3 mL per injection) under gentle stirring at 30-minute intervals. The reaction mixture was allowed to react at 33 °C for 12 h. The synthesized product was centrifuged (12,000 rpm, 15 min) and re-dispersed in ethanol. 按照如上方法包覆后离心一次分散在水中没问题，但是吸收峰是蓝移的，分散在乙醇中立马颜色变为紫蓝色，测UV吸收峰发现没有吸收峰了。请问问题出在哪儿呢？ |
回复此楼» 猜你喜欢
稀土发光分析｜核壳结构｜寿命拟合
已经有6人回复
-
稀土发光分析｜核壳结构｜寿命拟合
已经有0人回复
-
金属材料论文润色/翻译怎么收费?
已经有285人回复
-
稀土发光分析｜核壳结构｜寿命拟合
已经有0人回复
-
26 届青岛大学纺织化学与染整工程硕士（液体纳米分散染料方向）求申博建议
已经有4人回复
-
26 届青岛大学纺织化学与染整工程（液体纳米分散染料）求浙理工纺织 / 材料博导名额
已经有1人回复
-
敢问Acta Pharmaceutica Sinica B with Editor 三周了，能是什么情况？
已经有0人回复
-
求助 CeO2 Fe3O4 Cu2S CoFe2O4 标准卡 Jade 导出的数据
已经有0人回复
-
求助一篇MEMS散热器件文献
已经有0人回复
-
材化专业SCI论文（职称评定）
已经有0人回复
款款飞
木虫 (著名写手)
- 应助: 1 (幼儿园)
- 金币: 12543.6
- 散金: 550
- 红花: 4
- 帖子: 2423
- 在线: 434.4小时
- 虫号: 421711
- 注册: 2007-07-14
- 专业: 概率论与随机分析
4楼2017-10-17 09:49:14
 本帖仅楼主可见 |
2楼2017-10-15 19:11:09
款款飞
木虫 (著名写手)
- 应助: 1 (幼儿园)
- 金币: 12543.6
- 散金: 550
- 红花: 4
- 帖子: 2423
- 在线: 434.4小时
- 虫号: 421711
- 注册: 2007-07-14
- 专业: 概率论与随机分析
3楼2017-10-17 09:48:22
xingdao
金虫 (著名写手)
- 应助: 2 (幼儿园)
- 金币: 1440.9
- 散金: 2148
- 红花: 17
- 帖子: 1185
- 在线: 484.8小时
- 虫号: 2528893
- 注册: 2013-07-02
- 性别: GG
- 专业: 金属材料的制备科学与跨学
5楼2017-10-17 20:43:01
20