二氧化硅包覆金棒后离心无法溶解在乙醇中的问题
|
|
请教各位，我用二氧化硅包覆金棒，参考的文献的方法是：the CTAB surfactants in the crude GNRs suspension (200 mL) were removed via two cycles of centrifugation/rinsing (12000 rpm, 15 min), and then re-dispersed in 50 mL Milli-Q water. Subsequently, it was transferred into an aqueous solution of CTAB (250 mL, 0.8 mM), and KOH solution (0.1 M) was added to adjust the pH value to ca. 10. After equilibration at 33 °C for 30 min, a solution of TEOS/APTES/ethanol (0.9 mL, 1/0.05/4 vol.) was added into the mixture by three times (0.3 mL per injection) under gentle stirring at 30-minute intervals. The reaction mixture was allowed to react at 33 °C for 12 h. The synthesized product was centrifuged (12,000 rpm, 15 min) and re-dispersed in ethanol. 按照如上方法包覆后离心一次分散在水中没问题，但是吸收峰是蓝移的，分散在乙醇中立马颜色变为紫蓝色，测UV吸收峰发现没有吸收峰了。请问问题出在哪儿呢？ |
回复此楼» 猜你喜欢
求助Fe-TCPP、Zn-TCPP的CIF文件，或者CCDC号
已经有0人回复
-
XPS/?λXPS
已经有0人回复
-
金属材料论文润色/翻译怎么收费?
已经有274人回复
-
河北大学-26年秋季入学化学博士招生
已经有0人回复
-
招收2026年入学博士研究生
已经有10人回复
-
哈尔滨工程大学材化学院国家级青年人才-26年硕士招生
已经有2人回复
 本帖仅楼主可见 |
2楼2017-10-15 19:11:09
款款飞
木虫 (著名写手)
- 应助: 1 (幼儿园)
- 金币: 12550.6
- 散金: 550
- 红花: 4
- 帖子: 2421
- 在线: 434.3小时
- 虫号: 421711
- 注册: 2007-07-14
- 专业: 概率论与随机分析
3楼2017-10-17 09:48:22
款款飞
木虫 (著名写手)
- 应助: 1 (幼儿园)
- 金币: 12550.6
- 散金: 550
- 红花: 4
- 帖子: 2421
- 在线: 434.3小时
- 虫号: 421711
- 注册: 2007-07-14
- 专业: 概率论与随机分析
4楼2017-10-17 09:49:14
xingdao
金虫 (著名写手)
- 应助: 2 (幼儿园)
- 金币: 1438.9
- 散金: 2148
- 红花: 17
- 帖子: 1185
- 在线: 484.8小时
- 虫号: 2528893
- 注册: 2013-07-02
- 性别: GG
- 专业: 金属材料的制备科学与跨学
5楼2017-10-17 20:43:01
10