| 查看: 1300 | 回复: 3 | ||
[求助]
XPS表征 已有1人参与
|
|
审稿中审稿人对我提出这样的意见a) That is, the main signals are the Ni 2p3/2 components, that in your case it is seen three components/bands (Nid+, Ni2+ and shake-up satellite), and therefore you should see other three bands associated to the main ones, which should be separated according to the data found in the literature and also maintaining a fixed area ratio. b) P 2p decomposition. I also see different FWHM of bands associated to the same species. The same FWHM should be used for all the spectra. The same decomposition used for Ni2PN/M41 should be employed for Ni2PO/M41 but with different ratios. It is obvious that different P species are present on the surface depending on the pretreatment employed. The decomposition should be redone. 请问审稿人的意思是什么啊？我哪里分的不好呢  Fig.5(a).jpg  Fig.5(b).jpg |
回复此楼» 猜你喜欢
瑞典林雪平大学范立洲课题组现招聘博士后、岗位制博士生
已经有0人回复
-
中国科大仿生界面材料科学全国重点实验室戴懿涛研究员/江雷院士团队招聘科研助理
已经有0人回复
-
物理化学论文润色/翻译怎么收费?
已经有90人回复
-
中国科大仿生界面材料科学全国重点实验室戴懿涛研究员/江雷院士团队招聘科研助理
已经有0人回复
-
寻求物理化学学报最新的投稿模板！
已经有4人回复
-
东南大学杰青/海优团队招聘催化方向博士后
已经有866人回复
-
投稿咨询
已经有7人回复
-
自科面上 散金币 祈福
已经有61人回复
-
铁钼催化剂成型
已经有2人回复
-
求问：LATP煅烧应该使用什么容器？
已经有0人回复
-
西安交通大学 赵旭课题组 招收研究助理--电催化方向
已经有0人回复
【答案】应助回帖
感谢参与，应助指数 +1
|
XPS分峰时有一些最基本的限制条件。 2p3/2的峰和相应2p1/2的峰的面积比是2:1，这个必须在分峰时加以限制。你的Ni2p中有Ni2p3/2的三个峰和Ni2p1/2的三个峰，相对应的峰应有2:1的面积比关系。 其次，同一元素应有相同的半峰宽，因为这是由x-ray本身，单色器还有分析器的分辨力决定的。同一元素的不同化学态，自旋轨道分裂的峰都应是相同的半峰宽。如果拟合不好，说明还有其他的化学态包含在峰里，当然也可能是峰型选得不好或者背景扣除的不好的原因。 总之，XPS分峰要加以诸多的物理限制来取得真正具有物理意义的分峰。不加以限制，虽然会拟合得很好，但是只有数学意义。 |
2楼2015-03-14 09:48:45
3楼2015-03-16 13:49:14
4楼2018-06-19 10:05:34