[求助]
XPS表征 已有1人参与
|
|
审稿中审稿人对我提出这样的意见a) That is, the main signals are the Ni 2p3/2 components, that in your case it is seen three components/bands (Nid+, Ni2+ and shake-up satellite), and therefore you should see other three bands associated to the main ones, which should be separated according to the data found in the literature and also maintaining a fixed area ratio. b) P 2p decomposition. I also see different FWHM of bands associated to the same species. The same FWHM should be used for all the spectra. The same decomposition used for Ni2PN/M41 should be employed for Ni2PO/M41 but with different ratios. It is obvious that different P species are present on the surface depending on the pretreatment employed. The decomposition should be redone. 请问审稿人的意思是什么啊？我哪里分的不好呢  Fig.5(a).jpg  Fig.5(b).jpg |
回复此楼» 猜你喜欢
吴鹏 杰青 博士春季招生
已经有2人回复
-
中国科学院大连化物所低碳战略中心发布RCESBot 科研智能体
已经有0人回复
-
物理化学论文润色/翻译怎么收费?
已经有186人回复
-
中科大国家杰青 路军岭老师 一个热催化方向的博士生名额
已经有0人回复
-
中科大国家杰青路军岭教授团队诚招热催化方向的博士生一名
已经有0人回复
-
一个化合物的合成路线：CAS:367929-02-0 名称：8β-乙烯基雌二醇
已经有4人回复
-
求助文献
已经有0人回复
-
招计算化学博士，要求本或研的学位计算机相关，英语六级，第一作者SCI或第一专利授权
已经有0人回复
-
东南大学废弃碳资源利用团队（杰青/海优团队）博士后、科研助理及27级博士生招募
已经有17人回复
-
东南大学废弃碳资源利用团队（杰青/海优团队）27级博士研究生和科研助理招生
已经有21人回复
【答案】应助回帖
感谢参与，应助指数 +1
|
XPS分峰时有一些最基本的限制条件。 2p3/2的峰和相应2p1/2的峰的面积比是2:1，这个必须在分峰时加以限制。你的Ni2p中有Ni2p3/2的三个峰和Ni2p1/2的三个峰，相对应的峰应有2:1的面积比关系。 其次，同一元素应有相同的半峰宽，因为这是由x-ray本身，单色器还有分析器的分辨力决定的。同一元素的不同化学态，自旋轨道分裂的峰都应是相同的半峰宽。如果拟合不好，说明还有其他的化学态包含在峰里，当然也可能是峰型选得不好或者背景扣除的不好的原因。 总之，XPS分峰要加以诸多的物理限制来取得真正具有物理意义的分峰。不加以限制，虽然会拟合得很好，但是只有数学意义。 |
2楼2015-03-14 09:48:45
3楼2015-03-16 13:49:14
4楼2018-06-19 10:05:34