[求助]
英语论文翻译，求助！大神帮帮忙！
|
|||
|
2.2. Synthesis of graphite oxide Graphite oxide was synthesized through a modified Hummers method [30] from nature graphite flake. 2 g of graphite and 1 g of NaNO3 were dissolved in 46 mL of concentrated H2SO4 under an ice bath. After about 15 min of stirring, 6 g of KMnO4 was gradually added into the suspension with stirring as slowly as possible in order to control the reaction temperature below 20 ◦C. The suspension was stirred for 2 h, and then maintained at 35 ◦C for 30 min. 92 mL of deionized water was slowly poured into the suspension,resulting in a quick increase in temperature, and the temperature should be controlled lower than 98 ◦C. After 15 min, the suspension was then further diluted to approximately 280 mL with warm deionized water. 20 mL of 30% H2O2 was added for the purpose of removing the residual KMnO4 and MnO2 to change the color into luminous yellow. Then, the suspension was filtered and washed with warm 5% HCl aqueous solution and deionized water, respectively, until no sulfates were detected and the pH of the filtrate was adjusted to 7. The sample of graphite oxide was dried under vacuum at 50 ◦C to a constant weight, and then milled to an ideal particle size. |
回复此楼» 猜你喜欢
277材料科学与工程080500求调剂
已经有7人回复
-
317求调剂
已经有18人回复
-
293求调剂
已经有5人回复
-
280分求调剂 一志愿085802
已经有7人回复
-
0854电子信息求调剂
已经有3人回复
-
263求调剂
已经有4人回复
-
石河子大学（211、双一流）硕博研究生长期招生公告
已经有3人回复
-
一志愿西安交通大学材料工程专业 282分求调剂
已经有13人回复
-
北科281学硕材料求调剂
已经有6人回复
-
328求调剂，英语六级551，有科研经历
已经有10人回复
18236135970
银虫 (小有名气)
- 翻译EPI: 6
- 应助: 2 (幼儿园)
- 金币: 686.2
- 散金: 1150
- 红花: 2
- 帖子: 60
- 在线: 55.9小时
- 虫号: 3431437
- 注册: 2014-09-21
- 性别: GG
- 专业: 化学工程及工业化学
【答案】应助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
qa535758874: 金币+35, 翻译EPI+1, ★★★★★最佳答案, 非常感谢你的回复,我很满意，很棒！谢谢你哈！ 2015-03-08 18:02:54
qa535758874: 金币+35, 翻译EPI+1, ★★★★★最佳答案, 非常感谢你的回复,我很满意，很棒！谢谢你哈！ 2015-03-08 18:02:54
|
2.2 氧化石墨的合成 通过改良Hummers法利用天然石墨合成氧化石墨。冰浴条件下，将2g石墨和1g NaNO3溶解到46ml浓硫酸中，经过大约15min搅拌，6g KMnO4逐渐加入到悬浮液中，同时尽可能慢搅拌控制反应温度在20°C以下。悬浮液搅拌2h.然后在35°C下保持30min。92ml去离子水缓慢倒入悬浮液导致温度快速上升，温度应控制在98°C以下。经过15min，用温的去离子水将悬浮液进一步稀释到大约280ml。加入20ml 30％H2O2去除残留的KMmO4和MnO2，改变颜色至明亮的黄色。然后过滤悬浮液，用温5％HCl水溶液和去离子水清洗。相对来说，直到检测不出硫酸盐，滤出液PH大约为7。将氧化石墨样品在50°C真空条件下干燥至恒重，然后研磨至理想颗粒大小。 [ 发自手机版 https://muchong.com/3g ] |
2楼2015-03-03 21:07:19
18236135970
银虫 (小有名气)
- 翻译EPI: 6
- 应助: 2 (幼儿园)
- 金币: 686.2
- 散金: 1150
- 红花: 2
- 帖子: 60
- 在线: 55.9小时
- 虫号: 3431437
- 注册: 2014-09-21
- 性别: GG
- 专业: 化学工程及工业化学
3楼2015-03-03 21:32:11