luzhijian

金虫 (著名写手)

[交流] 【请教】关于审稿意见中XRD解释的一个小问题。

我是把Cu粉和Si3N4粉放在高能球磨机中进行球磨的,对图中的解释为

Figure 2 depicts the XRD patterns of as-milled Cu-25 wt% Si3N4 at different stages of milling. It was confirmed that only two phases of Cu and Si3N4 were present in the as-milled powders.

It was also found that with increasing the milling time, the diffraction peaks of Cu and Si3N4 became broader. This change revealed a reduced grain size and an elevated strain energy stored inside particles, because of the severe plastic deformation introduced during ball milling.

As the milling time increased, the diffraction peaks of the as-milled powders were rougher, suggesting that the deformation of the crystals became much stronger.  图中(a)3 h, (b) 7 h, (c) 9 h, and (d) 12 h。

审稿人提出 What is the meaning of "rougher" XRD peaks?

我该怎么回答,我本意为随着时间的延长,衍射峰越来越粗糙。用rough的比较级rougher来表示更粗糙,不知道合适不?有没跟合适的词来表达更粗糙的意思。

[ Last edited by luzhijian on 2008-5-30 at 09:09 ]
回复此楼

» 猜你喜欢

择善人而交, 择善书而读, 择善言而听, 择善行而从。
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

fulutang

金虫 (小有名气)


luzhijian(金币+1,VIP+0):强度减小,但峰高低不平更加剧烈了
可以这样说吗?As the milling time increased,the intensities of the diffraction peaks of the as-milled powders gradually decreased.
5楼2008-05-30 08:56:20
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
查看全部 10 个回答

hjhw9513

木虫 (著名写手)


luzhijian(金币+1,VIP+0):我知道衍射峰会宽化,但峰形随着时间的推移,更加不规则和高低不平了。
是不是晶粒变小,半峰宽变大了?
2楼2008-05-29 17:03:23
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

lulinsmann

木虫 (著名写手)

三无小小鸟


luzhijian(金币+1,VIP+0):峰形随着时间的推移,变得更加高低不平了。
别说英文了,中文都不太明白,啥叫衍射峰越来越“粗糙”?难道是指信噪比?
看你最强峰左侧的峰似乎变强了,直接说有些峰变强了不得了?
江湖背影
3楼2008-05-29 21:51:40
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

baoyanl

金虫 (知名作家)


luzhijian(金币+1,VIP+0):烦请你看下我的帖子,我把对xrd的解释全贴上来了。
太不专业了,那有说衍射峰粗糙的啊!你也是做机械合金化的,但用粗糙来说,显得多外行啊。球磨时间延长,衍射峰宽化,强度变弱,表明晶格畸变,这才是标准的用语啊!
4楼2008-05-29 23:50:06
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
普通表情 高级回复 (可上传附件)
最具人气热帖推荐 [查看全部] 作者 回/看 最后发表
[考研] 304求调剂(085602,过四级,一志愿985) +27 化工人999 2026-04-04 28/1400 2026-04-11 13:02 by 小晏唯
[考研] 269求调剂 +8 跪求收留。 2026-04-04 8/400 2026-04-11 10:50 by zhq0425
[考研] 288求调剂 +15 代fish 2026-04-09 16/800 2026-04-11 10:26 by wwj2530616
[考研] 297求调剂 +9 Kwgyz 2026-04-09 9/450 2026-04-11 10:09 by zhq0425
[考研] 293求调剂 +6 勇远库爱314 2026-04-08 6/300 2026-04-11 10:08 by zhq0425
[考研] 346,工科求调剂 +3 moser233 2026-04-09 3/150 2026-04-11 10:04 by zhq0425
[考研] 070300化学学硕311分求调剂 +17 梁富贵险中求 2026-04-04 19/950 2026-04-11 00:29 by wangjihu
[考研] 调剂 +12 卷卷卷心菜_ 2026-04-09 13/650 2026-04-10 22:36 by Ftglcn90
[考研] 求调剂 +16 MAX怅惘 2026-04-09 18/900 2026-04-10 20:24 by 小鬼喔~~
[考研] 266求调剂 +29 阳阳哇塞 2026-04-07 29/1450 2026-04-10 16:20 by 高维春
[考研] 085400电子信息类(川大控制工程)求调剂可跨专业 求老师联系 +3 626776879 2026-04-08 3/150 2026-04-09 16:05 by 猪会飞
[考研] 086004 求调剂 309 +7 Yin DY 2026-04-08 7/350 2026-04-09 13:59 by Delta2012
[考研] 0860004 求调剂 309分 +6 Yin DY 2026-04-09 6/300 2026-04-09 10:19 by 啊李999
[考研] 328求调剂 +17 lftmya 2026-04-07 18/900 2026-04-09 08:05 by 5268321
[考研] 283求调剂 +19 A child 2026-04-04 19/950 2026-04-08 14:26 by xingguangj
[考研] 336求调剂,一志愿中科大 +9 墨彧 yuyu 2026-04-06 9/450 2026-04-08 11:24 by 想读书的菌菌
[考研] 307求调剂 +3 所念及所望 2026-04-06 3/150 2026-04-06 17:30 by 土木硕士招生
[考研] 085405软件工程301分求调剂,专硕可跨专业,四六级已过 +3 静静想想 2026-04-05 3/150 2026-04-06 15:23 by nepu_uu
[考研] 考研调剂生寻找导师 +3 顾瞻考研啊 2026-04-05 3/150 2026-04-05 18:18 by 啵啵啵0119
[考研] 295求调剂 +4 A你好研究生 2026-04-04 5/250 2026-04-04 22:46 by yu221
信息提示
请填处理意见