[求助]
麻烦翻译一下吧，急需呢，是在是万分感谢啊，谢谢，拜托
|
||
|
The glass was prepared by hydrolysis and polycondensation of 25 ml of tetraethyl orthosilicate (TEOS) (Aldrich, 98%), 3.42 ml of triethyl phosphate (TEP)(Aldrich, 99%), and 16.53 g of Ca(NO3)2 4H2O (Aldrich, 99%), that is, stoichiometric amounts to obtain anominal composition (mole %) of SiO2 (58), CaO (36), and P2O5 (6). 2 n of HNO3 was used to catalyse theTEOS and TEP hydrolysis, using a molar ratio of H2O/ (TEOS+TEP)=8. Each reactant was consecutivelyadded in 1 h intervals under continuous stirring. Afterwards, the solution was introduced in a hermeticallysealed cylindrical Teflon container where it was allowed to gel at room temperature and then aged at 701C for 3days. The drying was carried out at 1501C for 52 h, having replaced the previous container lid with onefeaturing a hole 1mm in diameter. |
回复此楼» 猜你喜欢
售SCI一区T0P文章，我:8O.55.1.O.5.4,科目齐全,可+急
已经有5人回复
-
售SCI-T0P文章，我:8O.5.5.1.O.54,科目齐全,可+急
已经有7人回复
-
上海工程技术大学 激光智能制造课题组 2027级博士研究生招生
已经有6人回复
-
课题组招2027级博士 上海工程技术大学 激光智能制造方向
已经有6人回复
-
现代”学阀”该如何界定
已经有14人回复
-
求合成方法
已经有8人回复
-
师弟论文见刊大半年才想起来申请专利，还能抢救一下吗？
已经有4人回复
-
有机合成以后会不会被AI改变？做科研的虫友怎么看
已经有8人回复
-
我的奶奶
已经有3人回复
【答案】应助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
sunny1992720: 金币+20, 翻译EPI+1, ★★★★★最佳答案, 不错啊，谢谢你 2014-11-10 10:36:26
sunny1992720: 金币+20, 翻译EPI+1, ★★★★★最佳答案, 不错啊，谢谢你 2014-11-10 10:36:26
| 玻璃通过25mL四乙氧基硅烷（TEOS）(Aldrich, 98%)、3.42mL三乙基膦 (TEP)(Aldrich, 99%)和16.53 g Ca(NO3)2 4H2O (Aldrich,99%)的水解聚合得到，按化学计量比各成分的摩尔百分比(mole %)为SiO2 (58)、CaO (36)、P2O5 (6)。加入2n的硝酸催化TEOS和TEP水解，其中水与(TEOS+TEP)的摩尔比为8。在搅拌下反应物每隔一小时连续加入。随后将溶液加入到圆柱形四氟乙烯容器并密封，待溶液在室温下成胶后在70度老化三天。随后将密封盖换成一有孔盖（直径1mm）并在150度下干燥52个小时。 |