89333627金虫 (小有名气)
|
[求助]
英语高手 帮忙 修改 润色一个摘要
|
||
|
The present paper developed a molding process for a new kind of z-pins applicable to C/C composites. Polyvinyl alcohol (PVA) was adopted as the matrix of z-pins since it has few solid residues in inert high-temperature environment. Highly concentrated PVA aqueous solution was prepared to impregnate the carbon fiber bundle. And draw forming method from small-hole-cavity dies was used to mold PVA-matrix z-pins. Four z-pins with different resin content were made by four dies with cavity diameters of 0.50mm, 0.60mm, 0.70mm and 0.80mm respectively. The piercing processes and properties of the z-pins were analyzed by the tests of piercing them into carbon fiber laminated fabrics. The results show that the measured value of PVA resin volume content of the z-pins is slightly larger than the theoretical value. And the z-pin prepared in the molding die with cavity diameter of 0.70mm(P7) has the best piercing property. Its resin volume content is 45.6%. The maximum compressive stress in the whole piercing process of P7 is the lowest compared with the z-pins molded by the other dies, and there is little damage to the piercing tip of P7 after penetration. Besides, it could be at least fully pierce 9mm thick laminated fabrics. 主要 修改语法错误，灰常感谢！ |
回复此楼» 猜你喜欢
26年申博自荐-计算机视觉
已经有4人回复
-
考博
已经有4人回复
-
药化及相关博士的申请
已经有3人回复
-
一篇MDPI论文改变了学习工作和生活
已经有4人回复
-
一个化合物的合成路线：CAS:367929-02-0 名称：8β-乙烯基雌二醇
已经有4人回复
-
中国地质大学（北京）博士招生补录，数理学院材料科学与工程专业和材料与化工专业
已经有3人回复
-
收到国自然专家邀请后几年才会有本子送过来评
已经有3人回复
ssssllllnnnn 
至尊木虫 (知名作家)
Translator and Proofreader
- 翻译EPI: 1690
- 应助: 452 (硕士)
- 金币: 31580.9
- 红花: 100
- 帖子: 7681
- 在线: 19966.6小时
- 虫号: 3328089
- 注册: 2014-07-17
- 专业: 肿瘤发生
【答案】应助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
RXMCDM: 金币+1, 多谢应助！ 2014-08-04 17:03:10
89333627: 金币+50, 翻译EPI+1, ★★★★★最佳答案, 非常感谢！ 2014-08-13 11:02:44
RXMCDM: 金币+1, 多谢应助！ 2014-08-04 17:03:10
89333627: 金币+50, 翻译EPI+1, ★★★★★最佳答案, 非常感谢！ 2014-08-13 11:02:44
|
Very well-written abstract. The present paper developed a molding process for a new kind of z-pins applicable to C/C composites. Polyvinyl alcohol (PVA) was adopted as the matrix of z-pins since it has few solid residues in inert high-temperature environment. Highly concentrated PVA aqueous solution was prepared to impregnate the carbon fiber bundle. DRAW forming method from small-hole-cavity dies was used to mold PVA-matrix z-pins. Four z-pins with different resin content were made by four dies with cavity diameters of 0.50 mm, 0.60 mm, 0.70 mm and 0.80 mm(,) respectively. The piercing processes and properties of the z-pins were analyzed by the tests of piercing them into carbon fiber laminated fabrics. The results show(ed) that the measured value of PVA resin volume content of the z-pins (was) slightly larger than the theoretical value. And the z-pin prepared in the molding die with cavity diameter of 0.70 mm (P7) ha(d) the best piercing property. Its resin volume content (was) 45.6%. The maximum compressive stress in the whole piercing process of P7 (was) the lowest compared with the z-pins molded by the other dies, and there (was) little damage to the piercing tip of P7 after penetration. Besides (In addition), it could (be-be should be deleted) at least fully pierce 9 mm thick laminated fabrics. Last sentence: In addition, it could completely pierce laminated fabrics with a minimum thickness of 9 mm. |
2楼2014-08-04 02:26:00