[求助]
水热产物为什么“重新分散到一定量的水中，冷冻干燥”？
|
|||
|
看到carbon上2013年一篇水热水热制备Fe3O4/C的文献，其中实验部分： 0.9g glucose (C6H12O6) was dissolved in 40mL deionized water and 1.212g iron(III) nitrate enneahydrate (Fe(NO3)39H2O) was dissolved in 2mL deionized water. The above two aqueous solutions were then mixed together and ultrasonicated for 15min. The resulting mixed solution (37.5mL) was transferred into a 40mL Teflon-lined stainless steelautoclave, and then heated at190 C for 9h.Once cooled to room temperature naturally, the resulted solid was collected through centrifugation and washed thoroughly with deionized water for several times. Subsequently, the obtained product was redispersed into a certain amount of deionized water, and freeze dried to obtain Fe2O3 nanocrystals encapsulated ininterconnected carbon nanospheres (designated as Fe2O3@C nanospheres) ，再经后续烧结得到的Fe3O4/C纳米球。 为什么不是洗涤后直接真空干燥，而是“将水热产物重新分散到一定量水中，再冷冻干燥”（划线部分），这样有什么好处？大家指点一下吧！ |
回复此楼» 收录本帖的淘帖专辑推荐
 四氧化三铁纳米颗粒制备、修饰及包覆 |
» 猜你喜欢
南京晓庄学院绿色能源材料团队招生
已经有0人回复
-
北方工业大学储能技术-02电化学储能与氢能方向招收2026级二次调剂学生
已经有0人回复
-
无机化学论文润色/翻译怎么收费?
已经有197人回复
-
求助WO3.cif文件 对应PDF卡片 43-1035，单斜晶系 , P21/n 。
已经有2人回复
-
稀土发光分析｜核壳结构｜寿命拟合
已经有13人回复
-
稀土发光分析｜核壳结构｜寿命拟合
已经有6人回复
-
稀土发光分析｜核壳结构｜寿命拟合
已经有0人回复
-
稀土发光分析｜核壳结构｜寿命拟合
已经有0人回复
-
26 届青岛大学纺织化学与染整工程硕士（液体纳米分散染料方向）求申博建议
已经有3人回复
-
26 届青岛大学纺织化学与染整工程（液体纳米分散染料）求浙理工纺织 / 材料博导名额
已经有1人回复
» 本主题相关商家推荐: (我也要在这里推广)
3楼2013-11-23 20:00:18
风雨中恋着你
木虫 (职业作家)
秋天不会冷
- 应助: 23 (小学生)
- 金币: 2370.5
- 散金: 278
- 红花: 8
- 帖子: 3499
- 在线: 363.8小时
- 虫号: 2633285
- 注册: 2013-09-03
- 性别: GG
- 专业: 无机非金属基复合材料
2楼2013-11-23 19:39:39
4楼2013-11-23 20:05:24
5楼2013-11-24 17:18:52