[求助]
核壳催化剂制备过程原理
|
||
|
求大神指导，小弟刚接触此方面还不是很了解，最近看文献，有如下一段：（！）（（1）Preparation of Nickel Cores. A mixture of Ni(acac) 2 (0.77g, 3.0 mmol) and TOP (4.0 mL, 9.0 mmol) in oleylamine (20mL) was slowly heated from room temperature to 493 K for 15 min under an inert atmosphere and was allowed to stir at 493 K for 45 min. After the reaction, the resulting black mixture was cooled at room temperature, and the particles were precipitated by adding ethanol (40 mL) and centrifuging at 10000 rpm for 20 min. Finally, the nickel nanoparticles were dispersed in cyclohexane. 其中加粗部分加入乙醇是起什么作用呀？ （2）Synthesis of Ni(3 nm)@SiO2 Yolk-Shell Nanocatalysts. Cyclohexane (25 mL) was added into a mixture of igepal CO-630 (8.0 mL) and NH4OH aqueous solution (1.0 mL) and stirred for 10 min. The nickel particle dispersion in cyclohexane (25 mL, 60 mM with respect to the nickel precursor concentration) was added into the mixture and allowed to stir rapidly for 30 s. TMOS (1.0 mL) and C18TMS (1.0 mL) were added, and the mixture was stirred for 1 h at room temperature. The resulting Ni@SiO2 core -shell particles were precipitated by adding methanThe ethanol dispersion (30 mL) of the Ni@SiO2 core -shell particles (50 mM with respect to the nickel precursor concentration) was treated with hydrochloric acidol (10 mL), washed with ethanol thoroughly, and redispersed in ethanol. The ethanol dispersion (30 mL) of the Ni@SiO2 core -shell particles (50 mM with respect to the nickel precursor concentration) was treated with hydrochloric acid (10 mL, 0.45 M) at room temperature for 30 min. The product was collected by centrifugation at 10 000 rpm for 30 min and washed with ethanol thoroughly. After drying at room temperature, the powders were placed in the ceramic boat in a glass tube oven, heated at a ramping rate of 4 K/min to 773K, and calcined at 773 K for 2 h under a hydrogen flow of 200 cc/min. After calcination, the resulting powders were cooled to room tem-perature and immediately submerged into anhydrous ethanol (20 mL) under a hydrogen environment in order to prevent surface oxidation of the nickel cores. 其中加入盐酸的的作用是什么呀？ 求大神帮忙呀，小弟万分感激！！！ |
回复此楼» 猜你喜欢
淮北师范大学 化学与化工科学学院 电催化课题组还有1名硕士研究生招生名额
已经有0人回复
-
英文期刊求助
已经有3人回复
-
化学工程及工业化学论文润色/翻译怎么收费?
已经有94人回复
-
化学相关硕士研究生招收调剂-湖北师范大学 （快来捡漏，最新调剂信息，过国家线即可）
已经有1人回复
-
河南理工大学化学化工学院招收学硕调剂生
已经有0人回复
-
黑龙江科技大学化工 环境工程调剂
已经有22人回复
-
莆田学院环境与生物工程学院资源与环境专硕（环境工程方向） 开放调剂招生
已经有13人回复
-
浙江海洋大学石油化工与环境学院招收工科调剂生（学硕、专硕均可，线上面试）
已经有0人回复
-
浙江海洋大学石油化工学院接收工科调剂（学硕、专硕均可，近期线上面试）
已经有8人回复
-
浙江海洋大学石油与天然气工程专业接收工科调剂（13日早上截止，线上面试）
已经有0人回复
-
考研调剂～湖南工程学院材料与化工学院
已经有0人回复
» 本主题相关价值贴推荐，对您同样有帮助:
- 晶面暴露与催化剂的可还原性（H2-TPR）之间的联系
已经有30人回复
- 氧化铝或氧化硅作为催化剂的原理
已经有3人回复
- 怎么实验室小试中活性较高的催化剂研制成工业催化剂
已经有15人回复
- 壳单元如何设置厚度的增加方向
已经有8人回复
- 核壳催化剂的制备
已经有6人回复
- 催化剂制备过程技术（清晰，带书签PDF）
已经有861人回复
- 制备Cu ZrO2催化剂怎样加速抽滤过程
已经有7人回复
- 制备含钡的荧光粉（Ba2SiO4:Eu）时，为什么钡原料采用BaCO3，而不采用BaO
已经有4人回复
- 【求助】关于催化剂制备过程中晶化，陈化，老化的含义和区别
已经有7人回复
- 【求助】请教双金属催化剂比单金属催化剂的优越性有哪些
已经有17人回复
- 【分享】固体催化剂的制备
已经有54人回复
- 【求助】制备核壳型催化剂，壳层的厚度怎么计算呢？
已经有8人回复
- 【求助】关于核壳结构的制备
已经有24人回复
- 浸渍法制备催化剂的原理与特点（补充zyhou的加压浸渍法）
已经有298人回复
ThxVV
木虫 (著名写手)
- 应助: 28 (小学生)
- 金币: 1484.2
- 散金: 20
- 红花: 2
- 帖子: 2123
- 在线: 76.4小时
- 虫号: 2054003
- 注册: 2012-10-11
- 性别: GG
- 专业: 化学反应工程
8楼2013-11-13 10:52:58
2楼2013-09-06 08:09:38
3楼2013-09-08 18:37:59
4楼2013-09-09 10:14:27