[求助]
做Fe3O4@SiO2核壳结构，等待出现无定形SiO2的馒头峰，却等来。。。
|
|||
|
The as prepared nanoparticles(1 g) were dispersed in a mixture of 100 mL of ethanol and 20 mL of DOW. TEOS (2 mL) and ammonium hydroxide (2.5 mL) were added subsequently under vigorous mechanic stirring at room temperature. After keeping the stirring for 20 h, the obtained Fe3O4/SiO2 composites were washed with ethanol and water for three times and dried under vacuum overnight. Hereafter, the produced composite (1 g) and APTES (1 mL) were dispersed in 50 mL of toluene and stirred at room temperature for 24 h. 我是按照上述方法做的核壳结构，XRD图却如下 木虫里面虽然也有人出现过如此问题，但是他们是找不到峰http://muchong.com/bbs/viewthread.php?tid=4591762，据坛子里高手解释是SiO2layer太薄了，但是我这里很奇怪，出现的峰里面除了Fe3O4，其余的峰基本能对上 ZSM-39 crystalline phase SiO2( JCPDS No.47-0720) 2θ=~12.7°，~15. 1°，23.8°，28.5°出现的几个比较强的峰都基本能对上，如图中黄色所示。请问各位这是什么原因呢？顺便附上我的txt文件，望高手帮忙分析下！  QQ截图20130513094950.jpg |
回复此楼» 本帖附件资源列表
-
欢迎监督和反馈：小木虫仅提供交流平台，不对该内容负责。
本内容由用户自主发布，如果其内容涉及到知识产权问题，其责任在于用户本人，如对版权有异议，请联系邮箱：xiaomuchong@tal.com - 附件 1 : SiO2Fe3O4.txt
2013-05-13 10:02:57, 41.45 K
» 猜你喜欢
金属材料论文润色/翻译怎么收费?
已经有172人回复
11楼2013-05-17 13:28:49
gxytju2008
专家顾问 (文坛精英)
-
专家经验: +1654 - MN-EPI: 2
- 应助: 4104 (副教授)
- 贵宾: 0.053
- 金币: 47726.2
- 散金: 4089
- 红花: 503
- 帖子: 14991
- 在线: 7309.4小时
- 虫号: 1111232
- 注册: 2010-09-29
- 性别: GG
- 专业: 材料物理化学
- 管辖: 微米和纳米
2楼2013-05-13 10:09:41
nanofollower
专家顾问 (著名写手)
-
专家经验: +108 - MN-EPI: 2
- 应助: 411 (硕士)
- 贵宾: 0.005
- 金币: 5255
- 红花: 28
- 帖子: 1174
- 在线: 353小时
- 虫号: 2130741
- 注册: 2012-11-16
- 专业: 无机纳米化学
- 管辖: 微米和纳米
3楼2013-05-13 10:20:30
zihua886
铁杆木虫 (正式写手)
- 应助: 165 (高中生)
- 金币: 6451.3
- 散金: 25
- 红花: 29
- 帖子: 860
- 在线: 481.3小时
- 虫号: 1198268
- 注册: 2011-01-31
- 性别: GG
- 专业: 无机纳米化学
4楼2013-05-13 12:54:52