投的MSEA，有关铝合金材料在高温低周疲劳实验后的组织演化， 编辑回来的审稿意见，有一条是：
Experiments have been performed under total strain control. Rather stress control or plastic strain control would be expected. Why is total strain control used? Is there a technical reason for that?
Experiments have been performed under total strain control. Rather stress control or plastic strain control would be expected. Why is total strain control used? Is there a technical reason for that?
回复此楼