[求助] 纳米铜线的制备

关于合成铜纳米线，你们是采用的试剂有哪些？
具体点。各自有什么优缺点。

[ Last edited by kunpeng1782 on 2012-11-19 at 11:40 ]
回复此楼

» 收录本帖的淘帖专辑推荐

外语学习 科研经验与写作交流

» 猜你喜欢

» 本主题相关商家推荐: (我也要在这里推广)

» 本主题相关价值贴推荐，对您同样有帮助:
1楼 2012-11-19 10:51:30
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

ningmenguge

至尊木虫 (著名写手)
用杜克大学抄袭的方法，主要是 硝酸铜，氢氧化钠，EDA，hydrazine。
用xia的方法是，氯化铜，HDA,glucose。
还有用CTAB的，杜的方法主要是分散性差，xia的方法也是，分散性也不够理想。
建议你看看Synthesis of Ultralong Copper Nanowires for High-Performance
Transparent Electrodes这篇文章
Herein, we report a nonaqueous synthesis of ultralong single-c rys tal li ne Cu nan ow ire s wi th e xce ll en t di s pe rs ib il it y. Ou r
synthesis strategy relies on self-catalytic growth of Cu nanowires
within a liquid-crystalline medium of HDA and cetyltriamoni-num bromide (CTAB). HDA and CTAB are fi rst mixed at
elevated temperature to form a liquid-crystalline medium. Upon
addition of the precursor, copper acetylacetonate [Cu(acac)
2
],
ultralong nanowires with excellent dispersibility form sponta-neously within the medium in the presence of a catalytic Pt
surface.
赞一下(4人) 回复此楼
2楼2012-11-19 10:58:47
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

陈剑宇

铜虫 (小有名气)
引用回帖:
2楼: Originally posted by ningmenguge at 2012-11-19 10:58:47
用杜克大学抄袭的方法，主要是 硝酸铜，氢氧化钠，EDA，hydrazine。
用xia的方法是，氯化铜，HDA,glucose。
还有用CTAB的，杜的方法主要是分散性差，xia的方法也是，分散性也不够理想。
建议你看看Synthesis of  ...

,恩。
3楼2012-11-19 15:02:47
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

ningmenguge

至尊木虫 (著名写手)

【答案】应助回帖

★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ...
感谢参与，应助指数 +1
陈剑宇: 金币+80, ★★★很有帮助, 很不错 2012-11-19 15:18:03
也可以关注这篇Electrochemical synthesis of copper nanowires 新的方法，就是比较繁琐。

The potentiostatic ECD of the copper nanowires was performed in a conventional three-electrode bath containing a mixture of 0.2 M CuSO
4·5H2 O and 0.1 M H 3 BO3aqueoussolutions. The pH of the solution was controlled in the range 4.5–5.0 by adding 0.1 M H
2 SO4solution. A glassy carbon plate and a saturated calomel electrode (SCE) were used as counter-electrode and reference electrode, respectively. The copper ECD was carried out at different
applied potentials ( −0 .15, −0 .30, and −0 .45 V, SCE) for 20–30 min at room temperature to prepare the copper nanowires. After the ECD, the upper parts of the samples were polished by using a 50 nm SiC polishing sandpaper in order to remove the copper particles that had grown
excessively and stuck on the sample surface. Then the PAA template with copper nanowires was washed with ethanol and de-ionized water in turn, and dried in air before characterization
赞一下(1人) 回复此楼
4楼2012-11-19 15:08:42
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

luxinrong

新虫 (初入文坛)
引用回帖:
2楼: Originally posted by ningmenguge at 2012-11-19 10:58:47
用杜克大学抄袭的方法，主要是 硝酸铜，氢氧化钠，EDA，hydrazine。
用xia的方法是，氯化铜，HDA,glucose。
还有用CTAB的，杜的方法主要是分散性差，xia的方法也是，分散性也不够理想。
建议你看看Synthesis of  ...

这篇文献我也看过，是东大和别人合作的，按照那个试了好几次完全没有得到想要的东西啊，想想问题可能出在镀铂的硅片上，我是在硅片光滑的一面镀了大概10nm厚度的，请问应该用什么样子的？具体那个硅片怎么做？还有这个对无水无氧条件要求高吗？
赞一下 回复此楼
5楼2013-07-15 17:15:07
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

ningmenguge

至尊木虫 (著名写手)
引用回帖:
5楼: Originally posted by luxinrong at 2013-07-15 17:15:07
这篇文献我也看过，是东大和别人合作的，按照那个试了好几次完全没有得到想要的东西啊，想想问题可能出在镀铂的硅片上，我是在硅片光滑的一面镀了大概10nm厚度的，请问应该用什么样子的？具体那个硅片怎么做？还有 ...

恩，纳米级别的铜非常活泼，你不处理就氧化了。
赞一下 回复此楼