[交流] vasp计算AFM体系磁矩不为0，求解已有1人参与

在计算Mn2O反铁磁性结构优化时，最终得到的磁矩不为0，而是2.8449um，是由于在AFM体相中掺杂正电子体系，导致AFM受外电子场干扰总磁矩不为0吗？请大家帮忙分析下原因，较急！
以下为INCAR与OSZICAR：
------------------------------------------------------------------------------------------------------
INCAR：

ISTART = 0
ICHARG = 2

LREAL  = A
#  PREC = N          precision:Medium/High/Low
ENCUT  = 400
  EDIFF  = 1e-5             converge criterion: default=1e-4
  EDIFFG = -0.01
MAXMIX = 50
# ALGO  = N
NELM = 300
NELMIN = 5             the minimum number of electronic SC steps
IBRION = 2
NSW = 300
ISIF = 3
ISYM = 2                symmetry (2-PAW on, 1-US-PP's on, 0-off)
GGA = PE             Perdew-Wang 91
! LORBIT = 11
ISPIN = 2
MAGMOM =4*0 16*0 3 -3 3 -3 3 -3 3 -3 #原子顺序依次为：掺杂原子、O、Mn，最后8个Mn原子分别设置初始磁矩

LWAVE  = F
LCHARG = F
NWRITE = 2

ISMEAR = 0
SIGMA=0.1
----------------------------------------------------------------------------------------------------
输出的OSZICAR最后两个离子步为：
   N    E                   dE          d eps    ncg    rms       rms(c)
DAV: 1 -0.206981761686E+03 -0.30745E-05 -0.14674E-03  6156 0.155E-01 0.203E-02
DAV: 2 -0.206981760619E+03 0.10676E-05 -0.52135E-05  5664 0.359E-02 0.235E-03
DAV: 3 -0.206981760909E+03 -0.29068E-06 -0.30912E-06  3084 0.110E-02 0.157E-03
DAV: 4 -0.206981760961E+03 -0.52194E-07 -0.10091E-06  3108 0.657E-03 0.958E-04
DAV: 5 -0.206981760982E+03 -0.20709E-07 -0.47778E-07  3108 0.439E-03
  22 F= -.20698176E+03 E0= -.20696726E+03  d E =-.593441E-03  mag=    2.8396
   N    E                   dE          d eps    ncg    rms       rms(c)
DAV: 1 -0.206981820487E+03 -0.59526E-04 -0.50195E-02  6324 0.911E-01 0.131E-01
DAV: 2 -0.206982065301E+03 -0.24481E-03 -0.22599E-03  8964 0.251E-01 0.105E-01
DAV: 3 -0.206981951677E+03 0.11362E-03 -0.28856E-04  8808 0.102E-01 0.702E-02
DAV: 4 -0.206981900900E+03 0.50777E-04 -0.20869E-04  9768 0.822E-02 0.216E-02
DAV: 5 -0.206981900159E+03 0.74151E-06 -0.25365E-05  4164 0.262E-02
  23 F= -.20698190E+03 E0= -.20696739E+03  d E =-.139177E-03  mag=    2.8449