lkzmaster

木虫 (著名写手)

教授

[交流] 【求助】XPS 高手请忙帮

我的论文审稿意见中有这么一条In the Experimental Section, procedure for preparation of samples for XPS studies is to be described in more details. It seems that authors supported powders on double -sided scotch, which precludes any pretreatment of samples before spectra recording. In this case, the surface of samples is known to be hydroxylated, covered by carbonates and adsorbed CHx species trapped from air. Carbonates are also well known to be trapped in the bulk of high-surface-area ceria samples. Organic species trapped from air could reduce the surface even at room temperature especially during sample evacuation before measurements or under effect of the electron flood gun. All this makes difficult (if possible at all) reliable interpretation of XPS spectra in both O1s and Ce 3d ranges. Moreover, for sample studied after redox cycles, its inevitable transfer from reactor into the spectrometer through the air also affects its surface state even if it was reoxidized in the reactor before discharging (not mentioned, by the way). Hence, XPS data interpretation is certainly to be supported by experiments with sample supported on a metal holder which allows pretreatment in controlled conditions providing reproducible state of the surface.  If it is not possible for authors, I would advise just to remove this part of research from the article.
好像是说样品没有预处理,我是送样做的,对XPS的预处理知道的不多,看了半天还是不太明白这个审稿意见的意思,请XPS有经验的朋友帮忙看看。谢谢了!
回复此楼
有多少梦想可以重来
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

linqi723

铁杆木虫 (著名写手)


小木虫(金币+0.5):给个红包,谢谢回帖
引用回帖:
1楼: Originally posted by lkzmaster at 2010-10-15 10:21:14:
我的论文审稿意见中有这么一条In the Experimental Section, procedure for preparation of samples for XPS studies is to be described in more details. It seems that authors supported powders on double - ...

刚你站内信问问,奈何找不到如何回复你,所以在此 文不对题的发图。见谅

auto 可以实现曲线的完全分离,
如果觉得效果不好,或想减小分开度
,可以 双击图层
在 刚才 auto分离的基础上,用individual
2013
9楼2012-03-02 14:16:38
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

linqi723

铁杆木虫 (著名写手)

★ ★
小木虫(金币+0.5):给个红包,谢谢回帖
lkzmaster(金币+1): 非常感谢,不知道小木虫什么问题,你第一次给我的信息是和第二次一起到的,所以第一次的没有及时回复,非常抱歉。这个帖子只有一个金币了,不好意思。 2012-03-07 10:39:06
引用回帖:
9楼: Originally posted by linqi723 at 2012-03-02 14:16:38:
刚你站内信问问,奈何找不到如何回复你,所以在此 文不对题的发图。见谅

auto 可以实现曲线的完全分离,
如果觉得效果不好,或想减小分开度
,可以 双击图层
在 刚才 auto分离的基础上,用individual

弄错了,应该是上传图片 不是附件,sorry

1  原始图



2 auto 快速偏移分开






auto分开效果



auto分开效果不满意? 可以 切换到individual 模式,进行微调



微调Y 轴偏移量



微调 数值  appy 可以 看到效果