这是什么制备工艺?
|
||
| gas pressure infiltration |
回复此楼» 猜你喜欢
材料专硕283求调剂
已经有15人回复
-
求调剂
已经有14人回复
-
（调剂）一志愿报考哈尔滨工业大学0857资源与环境专业378分考生
已经有3人回复
-
本科211，293分请求调剂
已经有9人回复
-
315求调剂
已经有4人回复
-
308求调剂
已经有4人回复
-
301求调剂
已经有4人回复
-
304求调剂
已经有5人回复
-
302分 085601求调剂推荐
已经有9人回复
-
一志愿9材料学硕297已过六级求调剂推荐
已经有12人回复
4楼2010-04-19 21:51:57
shmily5368(金币+2, 翻译EPI+1): 2010-04-19 21:21
|
Gas pressure infiltration (GPI) is process for preparation of composite materials where molten matrix material is infiltrated into the pores of preform under the influence of high gas pressure. Technology usually has several steps: evacuation of pressure vessel (some material as Mg are heated under protective gas because of the evaporation which can damage equipment), heating under vacuum until matrix material is melted, immersion of porous preform into the melt, infiltration under high pressure and withdrawal of the sample from the melt (in case of some material systems were wettability is not sufficient, sample solidifies together with matrix in crucible). In some cases bonding between constituents is established due to the chemical reaction at the interface (for example formation of carbides), but sometimes this bond is only mechanical. Cross section of typical gas pressure infiltration equipment showing pressure vessel, insulation of the pressure vessel, heating element and crucible which is used for material melting Steps of gas pressure infiltration process: a) porous preform above matrix material during heating; b) immersion of porous preform into the molten matrix material and inlet of pressurized gas; c) infiltrated sample in molten matrix and d) withdrawal of infiltrated sample from the melt As mentioned before, terms which are very often related with gas pressure infiltration technology are wettability or wetting angle. Wetting is determinated by contact angle between liquid phase and solid substrate. GPI process is used because in some cases wetting angle between molten matrix and solid porous reinforcement is relatively high. To overcome this problem high pressure must be used. If wetting angle is 90° or lower, this is considered as good. Sometime, wetting angle between constituents is so high (pure copper/carbon fibres) that not even extremely high pressure cannot ensure good infiltration results |
2楼2010-04-19 19:38:13
shmily5368
银虫 (小有名气)
- 应助: 0 (幼儿园)
- 金币: 1329.5
- 散金: 20
- 帖子: 100
- 在线: 13.8小时
- 虫号: 800905
- 注册: 2009-06-29
- 专业: 结构陶瓷
3楼2010-04-19 21:20:50
5楼2010-04-19 21:52:08