[交流]
帮看看这段话的语法
|
|||
| TiO2 electrochromic coatings were successfully fabricated by the MAO method on commercially pure titanium substrates in Al(OH)3 colloidal solution. The coating surface morphology becomes coarser with increasing the voltage. The coatings were completely consisted of rutile TiO2, no other TiO2 phases been detected. During the cyclic voltammetry sweeps, the coatings show good reversibility between blue coloration and bleaching cycles in pH 2.0 HCl solutions. The cyclic voltammograms indicates that the coatings work well as an electrochromic material, and the MAO is a feasible method to fabricate TiO2 electrochromic coatings. Considering the microstructure and cyclic voltammograms of the coatings, the voltage has some great impact on the characteristic of the coatings. |
回复此楼» 猜你喜欢
参与限项
已经有3人回复
-
假如你的研究生提出不合理要求
已经有7人回复
-
实验室接单子
已经有4人回复
-
全日制（定向）博士
已经有4人回复
-
对氯苯硼酸纯化
已经有3人回复
-
求助:我三月中下旬出站，青基依托单位怎么办？
已经有12人回复
-
不自信的我
已经有12人回复
-
所感
已经有4人回复
-
要不要辞职读博？
已经有7人回复
-
北核录用
已经有3人回复
priorpost06
至尊木虫 (著名写手)
- 应助: 11 (小学生)
- 金币: 12220
- 散金: 7
- 红花: 7
- 帖子: 1607
- 在线: 522.7小时
- 虫号: 860480
- 注册: 2009-09-30
- 专业: 微生物生理与生物化学
4楼2010-01-04 23:11:32
legendyxg
木虫 (正式写手)
- 应助: 0 (幼儿园)
- 金币: 4428.9
- 散金: 129
- 红花: 2
- 帖子: 335
- 在线: 137.1小时
- 虫号: 933879
- 注册: 2009-12-27
- 性别: GG
- 专业: 工程热物理相关交叉领域
★ ★ ★ ★ ★
zap65535(金币+5,VIP+0):鼓励新虫+助人为乐 1-4 23:00
zap65535(金币+5,VIP+0):鼓励新虫+助人为乐 1-4 23:00
|
将商用的纯钛基在Al(OH)3胶体溶液中通过MAO方法成功的加工了电色涂层。随着电压的增加，涂层表面形貌变得更加粗糙。该涂层仅有金红石TiO2，没有发现其他任何相的tio2。在进行循环伏安法扫描过程中，该涂层在PH值为2.0的HCL溶液中在蓝色着色和漂白之间表现出了很好的可逆性。循环伏安法结果表明，该涂层作为一电色材料表现良好，从而表明MAO方法是加工tio2电色涂层的很容易的方法。考虑到涂层的微观结构和循环伏案特性，电压对该涂层的性能有着很大的影响。 大体上是这个意思，专业词汇上可能翻译有误，请谅解！ |
2楼2010-01-04 15:49:48
zap65535
木虫 (著名写手)
两院大学士后
- 翻译EPI: 9
- 应助: 2 (幼儿园)
- 贵宾: 0.711
- 金币: 1507.7
- 散金: 887
- 红花: 2
- 帖子: 1820
- 在线: 157.1小时
- 虫号: 704450
- 注册: 2009-02-19
- 性别: GG
- 专业: 马克思主义思想史
3楼2010-01-04 22:19:05
★ ★ ★ ★ ★ ★ ★ ★ ★ ★
ouyangshunli(金币+10,VIP+0): 1-6 20:35
ouyangshunli(金币+10,VIP+0): 1-6 20:35
|
The coating surface morphology became coarser when the voltage was kept increasing. The coatings were completely consisted of rutile TiO2, and no other TiO2 phases were detected. During the cyclic voltammetry sweeps, the coatings showed good reversibility between blue coloration and bleaching cycles in pH 2.0 HCl solutions. Considering the microstructure and cyclic voltammograms of the coatings, the voltage has great impact on the characteristic of the coatings. |
5楼2010-01-05 15:30:06