求助修改一段英语语法错误
|
||
| Large size single crystals of spinel Zn2TiO4 with 4-6mm in diameter and 30mm in length have been grown by the optical floating zone method for the first time. The results of X-ray diffraction and room temperature Raman spectrum show that the grown Zn2TiO4 crystal have a spinel-type structure without any impurity. The orientation of the Zn2TiO4 crystal was measured by the Bruker AXS D8 Discover X-ray diffractometer with GADDS (XRD2). Only one peak at 42.5° that can be indexed to the (400) direction was observed in the XRD2 pattern of the Zn2TiO4 wafer cut perpendicular to the growth direction. All results indicate that grown along the a-axis direction and high-quality Zn2TiO4 single crystal was successful grown by the optical floating zone method. |
回复此楼» 猜你喜欢
天津大学招2026.09的博士生，欢迎大家推荐交流（博导是本人）
已经有3人回复
-
有时候真觉得大城市人没有县城人甚至个体户幸福
已经有6人回复
-
面上项目申报
已经有3人回复
-
酰胺脱乙酰基
已经有9人回复
-
CSC & MSCA 博洛尼亚大学能源材料课题组博士/博士后招生｜MSCA经费充足、排名优
已经有5人回复
-
博士延得我，科研能力直往上蹿
已经有7人回复
-
退学或坚持读
已经有27人回复
-
面上基金申报没有其他的参与者成吗
已经有5人回复
-
遇见不省心的家人很难过
已经有22人回复
★ ★ ★ ★ ★ ★ ★ ★
ll921(金币+8,VIP+0):非常的感谢 12-31 08:54
ll921(金币+8,VIP+0):非常的感谢 12-31 08:54
|
Single crystals of spinel Zn2TiO4 with large size (4-6mm in diameter and 30mm in length ) were grown by the optical floating zone method for the first time. The results of X-ray diffraction and Raman spectrum showed that the prepared Zn2TiO4 crystal had a spinel-type structure without any impurity. Only one peak at 42.5° was observed in the XRD2 pattern. It could be indexed to the (400) direction of the Zn2TiO4 which was perpendicular to the growing direction. All results indicated that high-quality Zn2TiO4 single crystal growing along the a-axis direction was successful prepared by the optical floating zone method. 中间这句The orientation of the Zn2TiO4 crystal was measured by the Bruker AXS D8 Discover X-ray diffractometer with GADDS (XRD2). 完全可以不要，楼主看这样该可以不？ |
2楼2009-12-30 15:46:17
★ ★ ★ ★ ★ ★ ★ ★
ll921(金币+8,VIP+0):非常感谢！ 12-31 08:55
ll921(金币+8,VIP+0):非常感谢！ 12-31 08:55
|
Large size (Large-sized) single crystals of spinel Zn2TiO4 with 4-6mm in diameter and 30mm in length (既然有了直径，这里用thickness如何) have been grown by the optical floating zone method for the first time. The results of X-ray diffraction （这一句改成，The X-ray diffraction pattern）and room temperature(改成RT-recorded) Raman spectrum show that the grown （改成as-grown）Zn2TiO4 crystal（改成crystals） have a spinel-type structure without any impurity. The orientation of the Zn2TiO4 crystal was measured（取向用detected或者probed比较好一点） by the Bruker AXS D8 Discover X-ray diffractometer with GADDS (XRD2). Only one peak at 42.5° that can be （that can be去掉）indexed to the (400) direction was observed in the XRD2 pattern of the Zn2TiO4 wafer cut perpendicular to the growth direction. All results indicate that grown along the a-axis direction and high-quality Zn2TiO4 single crystal was successful grown by the optical floating zone method.(这一句改成All the results indicate that the high-quality Zn2TiO4 single crystal grown along the a-axis direction was successfully achieved using the optical floating zone method) ) |
3楼2009-12-30 16:37:06