tjpu302木虫 (正式写手)
Niu_HT
|
[交流]
【求助】纳米纤维的BET结果分析
|
|
|
t-method 计算没有微孔， 而DR,HK, SF都计算出微孔，应该用哪个？在小木虫看到t-method, DR,HK, SF都是分析微孔的方法，他们有什么区别和特别的应用吗？ BJH Method Cumulative Adsorption Pore Volume 怎么会比总的孔容 Total Pore Volume for pores 还大？ 以前没做过这方面分析，请专家帮忙分析一下？ SURFACE AREA DATA Multipoint BET.............................................. 9.974E+01 m²/g Single Point BET............................................ 8.701E+01 m²/g Langmuir Surface Area....................................... 1.817E+02 m²/g BJH Method Cumulative Adsorption Surface Area............... 1.991E+02 m²/g BJH Method Cumulative Desorption Surface Area............... 8.357E+01 m²/g DH Method Cumulative Adsorption Surface Area................ 2.079E+02 m²/g DH Method Cumulative Desorption Surface Area................ 8.732E+01 m²/g t-Method External Surface Area.............................. 9.974E+01 m²/g t-Method Micro Pore Surface Area............................ 0.000E+00 m²/g DR Method Micro Pore Area................................... 1.523E+02 m²/g PORE VOLUME DATA Total Pore Volume for pores with Diameter less than 7881.2 Å at P/Po = 0.99757........................ 1.072E-01 cc/g BJH Method Cumulative Adsorption Pore Volume................ 1.450E-01 cc/g BJH Method Cumulative Desorption Pore Volume................ 7.384E-02 cc/g DH Method Cumulative Adsorption Pore Volume................. 1.439E-01 cc/g DH Method Cumulative Desorption Pore Volume................. 7.338E-02 cc/g t-Method Micro Pore Volume.................................. 0.000E+00 cc/g DR Method Micro Pore Volume................................. 5.412E-02 cc/g HK Method Cumulative Pore Volume............................ 3.255E-02 cc/g SF Method Cumulative Pore Volume............................ 3.395E-02 cc/g PORE SIZE DATA Average Pore Diameter....................................... 4.300E+01 Å BJH Method Adsorption Pore Diameter (Mode).................. 1.380E+01 Å BJH Method Desorption Pore Diameter (Mode).................. 1.946E+01 Å DH Method Adsorption Pore Diameter (Mode).................. 1.380E+01 Å DH Method Desorption Pore Diameter (Mode).................. 1.946E+01 Å DR Method Micro Pore Width .............................. 1.813E+02 Å DA Method Pore Diameter (Mode)............................. 1.880E+01 Å HK Method Pore Width (Mode)............................. 1.362E+01 Å SF Method Pore Diameter (Mode)............................. 2.547E+01 Å 本帖关键词：Adsorption Pore BET Volume Method |
回复此楼
fdgudong
铁杆木虫 (正式写手)
- 应助: 25 (小学生)
- 金币: 6557.7
- 散金: 313
- 红花: 7
- 帖子: 829
- 在线: 189.3小时
- 虫号: 780052
- 注册: 2009-05-26
- 性别: GG
- 专业: 催化化学
5楼2009-12-03 17:07:36
xiaonade
木虫 (小有名气)
- 应助: 0 (幼儿园)
- 金币: 1867.1
- 散金: 157
- 帖子: 148
- 在线: 23小时
- 虫号: 533967
- 注册: 2008-03-27
- 专业: 化学反应工程
★ ★ ★
小木虫(金币+0.5):给个红包，谢谢回帖交流
骑着蜗牛追火箭(金币+2,VIP+0):谢谢 12-3 17:12
小木虫(金币+0.5):给个红包，谢谢回帖交流
骑着蜗牛追火箭(金币+2,VIP+0):谢谢 12-3 17:12
|
1、固体材料比表面积大于1 m2/g ( BET；Langmuir)。 2、微孔分布：0.45 — 1.7 nm; 微孔孔容：0.0001 cm3/g（Horvath-Kawazoe、MP-Method）。 3、中孔分布：1.7 — 300 nm; 中孔孔容：0.0001 cm3/g （BJH-Method、t-Plot Method、DET Theory）。 以Kelvin方程为基础的方法（如BJH法）是与孔内毛细管凝聚现象相关的，所以 它们可应用于介孔分布分析，但不适用于微孔填充的描述，甚至对于较窄的介孔 也不正确。 • 其它的经典理论，即如杜平宁-兰德科维奇（DR）法，和半径验处理的方法（如 HK和SF法）仅致力于描述微孔填充而不能应用于中孔分析. 这样看来，你测得这个绝对可以排除T-method的影响了。 |
2楼2009-12-03 16:01:53
xiaonade
木虫 (小有名气)
- 应助: 0 (幼儿园)
- 金币: 1867.1
- 散金: 157
- 帖子: 148
- 在线: 23小时
- 虫号: 533967
- 注册: 2008-03-27
- 专业: 化学反应工程
3楼2009-12-03 16:05:42
tjpu302
木虫 (正式写手)
Niu_HT
- 应助: 0 (幼儿园)
- 金币: 2189.4
- 散金: 5
- 红花: 1
- 帖子: 587
- 在线: 181.2小时
- 虫号: 398159
- 注册: 2007-06-10
- 性别: GG
- 专业: 纤维
4楼2009-12-03 16:52:19