| Nanocrystalline cerium(IV) oxide (CeO2) powders have been prepared by adding hydrazine monohydrate to an aqueous solution of hydrous cerium nitrate (Ce(NO3)3z 6H2O), followed by washing and drying. The lattice parameter of the as-prepared powder is a = 0.5415 nm. The powder characteristics and sinterability of reactive CeO2 have been studied. The surface areas of powders that have been heated at low temperatures are high, and these surface areas do not decrease to 10 m2/g until the temperature is >1200°C. Crystallite size and particle size are strongly dependent on the heating temperature. Optimum sintered densities are obtained by calcining in the temperature range of 700°–800°C. Ceramics with almost-full density can be fabricated at a temperature as low as 1150°C. |
回复此楼» 猜你喜欢
面上项目申报
已经有3人回复
-
有时候真觉得大城市人没有县城人甚至个体户幸福
已经有5人回复
-
酰胺脱乙酰基
已经有9人回复
-
CSC & MSCA 博洛尼亚大学能源材料课题组博士/博士后招生｜MSCA经费充足、排名优
已经有5人回复
-
有70后还继续奋斗在职场上的吗？
已经有6人回复
-
博士延得我，科研能力直往上蹿
已经有7人回复
-
退学或坚持读
已经有27人回复
-
面上基金申报没有其他的参与者成吗
已经有5人回复
-
遇见不省心的家人很难过
已经有22人回复
  |
2楼2009-11-10 18:40:25
hy52x
木虫 (正式写手)
- 应助: 0 (幼儿园)
- 金币: 5363.3
- 散金: 34
- 红花: 1
- 帖子: 309
- 在线: 417小时
- 虫号: 894154
- 注册: 2009-11-05
- 性别: GG
- 专业: 高分子合成化学
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
小甲009(金币+30,VIP+0):非常感谢你 ，你 有空了再给我翻译这篇文章的结论，还有金币的 ！ 11-10 22:21
小甲009(金币+30,VIP+0):非常感谢你 ，你 有空了再给我翻译这篇文章的结论，还有金币的 ！ 11-10 22:21
| 氧化铈粉末可以通过把联氨一水合物加入到Ce(NO3)3z 6H2O的水溶液中，之后通过水洗和干燥而制备。已制备的粉末晶格参数是a=0.5415纳米。活性CeO2的粉末特性和烧结能力已经被研究。在低温下被加热的粉末表面积很高，该表面积知道温度达到1200度才会减少到10m2/g.晶体尺寸和颗粒尺寸取决于加热温度。最佳烧结密度可以通过在700-800度的范围内煅烧而获得。全密度的陶器可以再温度1150度下被焊接。Sample Text |