| 查看: 2117 | 回复: 1 | |||
dxyan木虫 (正式写手)
|
[求助]
MIL-101的合成及纯化
|
|
采用不用HF合成MIL-101(Cr)，参考文献：Chem. Mater. 2012, 24, 166。但是做了很久比表面上不去。2200左右。其中DMF洗部分也洗了3次，每次12小时，70度，但是比表面积也就2400。DMF洗涤后也用甲醇，丙酮各洗过3，4次。但是BET依旧不行，吸附仪活化也达到足够的时间。合成完后釜壁面有灰色的一层，在各种溶剂洗的过程中离心完后离心管底部有层灰色的，但是大部分是绿色。谁能帮忙分析一下会是什么原因。原料或者釜的原因吗？加HF酸的方法也试过了，水洗醇洗后，加入氟化铵，然后再水洗，醇洗。但是比表面都2000以下。氟化铵交换2次，BET才达到2200。求各位帮忙分析一下，谢谢！ Cr(NO3)3·9H2O (1.0 g, 2.5 mmol), terephthalic acid (0.42 g, 2.5 mmol), and deionized water (10 mL) were blended and briefly sonicated resulting in a dark blue-colored suspension. The suspension was placed in a Teflon-lined autoclave bomb and kept in an oven at 218 °C for 18 h. After the bomb cooled down to room temperature, the resultant fine green MIL-101 crystals were separated from water using a centrifuge and washed with water, methanol and acetone. The suspension in acetone was centrifuged and separated, the solids were placed in N, N-dimethylformamide (10 mL) and the suspension was sonicated for 10 min and then kept at 70 °C overnight. The resulting solids were separated by centrifugation, repeatedly washed with methanol and acetone, dried at 75 °C overnight, |
回复此楼» 猜你喜欢
求助几个团簇的cif
已经有0人回复
-
急求该反应的详细机理
已经有5人回复
-
无机化学论文润色/翻译怎么收费?
已经有213人回复
-
【Ei | Scopus 双检索】2026年智能交通与未来出行国际会议（CSTFM 2026）
已经有0人回复
-
【EI|Scopus 双检索】2026年第六届机器人与人工智能国际会议（JCRAI 2026）
已经有0人回复
-
zotero的advanced material模板没有更新，有人有新版的cls文件吗
已经有2人回复
-
【高校联合举办】2026年第五届服务机器人国际会议（ICoSR 2026）
已经有0人回复
-
深圳大学化学与环境工程学院超分子团队招收2026级申请-考核制博士生
已经有8人回复
-
中南大学化学化工学院易小艺教授课题组招收2026级博士研究生（第二轮）
已经有0人回复
-
求助
已经有0人回复
2楼2024-11-13 21:55:13
100