| Figure 9 shows the efficiency calculated using Eq. 3 for anatase films under different light intensities. The efficiency curves show a maximum for all the light intensity values. The value of the efficiency increases as the incident photon energy increases. The maximum values determined for the anatase phase were approximately 5.9%. In the case of rutile, the maximum efficiency value was determined to be 3.8%. The maximum was located at approximately 0.8 V for lamp nominal powers of 80, 100, and 150 W. The measurements conducted at a nominal power of 100 W (Io = 231 mW/cm2) showed the highest efficiencies followed by the 150 W measurements. All the values are applied voltages relative to the reference Ag/AgCl electrode . |
回复此楼» 猜你喜欢
应该是下周三26日公布了吧？
已经有3人回复
-
投稿咨询
已经有7人回复
-
今天放榜没戏了吧
已经有11人回复
-
我面上完蛋了
已经有5人回复
-
让我中一个面上吧！
已经有12人回复
-
基金啊基金
已经有4人回复
-
放榜前的不淡定
已经有13人回复
-
时间戳今天，20号变了
已经有4人回复
-
只有每年这种时候来逛逛小木虫
已经有24人回复
-
估计是周四
已经有3人回复
2楼2009-06-14 11:45:04
★ ★
xiao828(金币+2,VIP+0):谢谢 6-14 14:04
xiao828(金币+2,VIP+0):谢谢 6-14 14:04
|
Figure 9 shows the efficiency calculated using Eq. 3 for anatase films under different light intensities. The efficiency curves show a maximum for all the light intensity values. The value of the efficiency increases as the incident photon energy increases. The maximum values determined for the anatase phase were approximately 5.9%. In the case of rutile, the maximum efficiency value was determined to be 3.8%. The maximum was located at approximately 0.8 V for lamp nominal powers of 80, 100, and 150 W. The measurements conducted at a nominal power of 100 W (Io = 231 mW/cm2) showed the highest efficiencies followed by the 150 W measurements. All the values are applied voltages relative to the reference Ag/AgCl electrode . 图9所示，在不同光照强度下锐钛矿薄膜效率（电流效率，是吗？）根据公式3计算得到。对于所有光强，其效率曲线呈现出最大值。效率随入射光子能量增加而增大。锐钛矿相的最大效率值接近5.9%。对于金红石而言，其最大效率值为3.8%。对于灯管80，100，150瓦三种额定功率，最大值出现在0.8v附近。在100瓦额定功率下的实验测量显示（入射光强=231 mW/cm2），最大效率小于额定功率150瓦的那组实验。所有效率值是与参考电极Ag/AgC有关的外电压。 |
3楼2009-06-14 12:22:59
幽雅百合
银虫 (小有名气)
- 应助: 0 (幼儿园)
- 金币: 393.3
- 帖子: 131
- 在线: 9.8小时
- 虫号: 730629
- 注册: 2009-03-25
- 性别: MM
- 专业: 凝聚态物性 II ：电子结构
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
xiao828(金币+1):谢谢参与
xiao828(金币+16,VIP+0):谢谢 6-14 14:04
xiao828(金币+1):谢谢参与
xiao828(金币+16,VIP+0):谢谢 6-14 14:04
|
图9展示了在不同光照强度下由方程3计算出的锐钛矿薄膜的效率。对所有的光照强度值，效率曲线存在一个最大值。效率随着入射光子能量的增加而增大。在锐钛相，效率的最大值约为5.9%。在金红石相，效率的最大值约为3.8%。当照射灯的额定功率分别为80w、100w、150w时，效率都在大约0.8v处达到最大值。在额定功率为100w（入射光强=231 mW/cm2）的照射灯下的测量表明最大效率大于额定功率为150w的那组测量值。与Ag/AgCl参考电极相比，所有的电压值都是适用的 建议把图贴上来，翻得才会准确！efficiency不知道是不是翻成效率。 希望对你有所帮助！ |