CTAB和油酸钠合成高长径比金纳米棒
|
|||
|
最近在用13年发表在nano letters 上的Using Binary Surfactant Mixtures To Simultaneously Improve the Dimensional Tunability and Monodispersity in the Seeded Growth of Gold Nanorods这篇文献做高长径比的金纳米棒，就是用CTAB和油酸钠做双表面活性剂，具体方法如下：种子合成方法和传统方法一致，To prepare the growth solution, 7.0 g (0.037 M in the final growth solution) or 9.0 g (0.047 M in the final growth solution) of CTAB and a certain quantity of NaOL were dissolved in 250 mL of warm water (~50 °C) in a 1L Erlenmeyer flask (Tables S2-S5). The solution was allowed to cool down to 30 °C and 4 mM AgNO3 solution, as detailed in Tables S2-S5, was added. The mixture was kept undisturbed at 30 °C for 15 min after which 250 mL of 1 mM HAuCl4 solution 3 was added. The solution became colorless after 90 min of stirring (700 rpm) and a certain volume of HCl (37 wt. % in water, 12.1 M) was then introduced to adjust the pH (Tables S2-S5). After another 15 min of slow stirring at 400 rpm, 1.25 mL of 0.064 M ascorbic acid (AA) was added and the solution was vigorously stirred for 30 s. Finally, a small amount of seed solution was injected into the growth solution (Tables S2-S5). The resultant mixture was stirred for 30 s and left undisturbed at 30°C for 12 h for NR growth. The final products were isolated by centrifugation at 7,000 rpm for 30 min followed by removal of the supernatant. No size and/or shape-selective fractionation was performed. 合成出来的棒是红棕色，紫外图在下面，看紫外图小峰应该是没什么球杂质的，SEM图显示还是有挺多的球杂质，不知道有哪位大佬做过这个方法，望不吝赐教，多谢  金纳米棒紫外图。png  1.jpg  2.jpg |
回复此楼» 猜你喜欢
广东以理材料系碳点与功能材料课题组 — 2博士名额 / 科研助理
已经有11人回复
-
24考博孤注一掷，寄在了复试，但是还是想上一个学
已经有39人回复
-
无机化学论文润色/翻译怎么收费?
已经有166人回复
-
P4VP的GPC测试
已经有3人回复
-
求购商用高炉煤气精脱硫水解催化剂
已经有36人回复
» 本主题相关商家推荐: (我也要在这里推广)
» 抢金币啦！回帖就可以得到:
-
平平安安，健健康康！
+5/540
-
80后普通人 征婚 坐标重庆
+1/165
-
湖大粤港澳大湾区创新研究院 诚聘研究助理和实习生
+1/132
-
质谱分析的同学，欢迎成为我的第一个博士生，毕业至少1篇AC，助力科研起飞
+5/125
-
大湾区大学（筹）常建课题组招聘特任研究员-待遇优厚
+1/84
-
南方科技大学微纳米力学实验室招收力学、机械、材料等方向2025级推免硕士研究生多名
+1/79
-
华南理工大学微电子学院-周长见课题组诚招博士后
+1/56
-
上市公司高薪诚聘硕博研发管培生/研发工程师；坐标上海；”职”为你来
+1/37
-
中国科学院福建物质结构研究所招聘博后和副研究员
+1/36
-
香港大学化学系招聘过渡金属催化方向博士后
+1/32
-
计算机模拟分子互作以及优化分析服务人员招聘
+1/30
-
国自然青基祈福
+2/22
-
哈尔滨工业大学王志江团队招聘材料、电化学等背景硕士、博士
+1/11
-
Fully funded PhD position in power electronics and electric motor drives
+1/6
-
有人测过鲜虾虾的氧化指标MDA/TBA/硫代巴比妥酸值/丙二醛含量吗？
+1/5
-
铀酰离子处理后的dnazyme（DNA核酶）没有现象
+1/4
-
哈工大郑州研究院刘绍琴教授课题组诚招优秀人才加盟！长期有效
+1/3
-
24考博孤注一掷，寄在了复试，但是还是想上一个学
+2/2
-
深圳理工大学药学院殷勤课题组招聘有机合成或药物化学博士后
+1/2
-
金属氧化物薄膜空气退火和真空退火对表面粗糙度的影响
+1/1
+5/540
24楼2018-07-02 23:41:43
★
光能使者007(金币+1): 谢谢参与
光能使者007(金币+1): 谢谢参与
|
本帖内容被屏蔽 |
10楼2018-03-02 19:26:34
nanofellow
专家顾问 (著名写手)
-
专家经验: +207 - MN-EPI: 6
- 应助: 231 (大学生)
- 贵宾: 0.12
- 金币: 11364.5
- 帖子: 1848
- 在线: 494.9小时
- 虫号: 1176389
17楼2018-03-03 17:09:55
18楼2018-03-03 19:53:44
nanofellow
专家顾问 (著名写手)
-
专家经验: +207 - MN-EPI: 6
- 应助: 231 (大学生)
- 贵宾: 0.12
- 金币: 11364.5
- 帖子: 1848
- 在线: 494.9小时
- 虫号: 1176389
19楼2018-03-04 10:11:26
20楼2018-03-04 14:57:21
21楼2018-04-17 21:30:51
22楼2018-04-19 13:39:52
23楼2018-04-19 20:37:19
25楼2018-07-03 10:28:01
★
小木虫: 金币+0.5, 给个红包，谢谢回帖
小木虫: 金币+0.5, 给个红包，谢谢回帖
|
本帖内容被屏蔽 |
26楼2018-08-16 18:52:54
|
本帖内容被屏蔽 |
27楼2018-08-16 18:54:17
nanofellow
专家顾问 (著名写手)
-
专家经验: +207 - MN-EPI: 6
- 应助: 231 (大学生)
- 贵宾: 0.12
- 金币: 11364.5
- 帖子: 1848
- 在线: 494.9小时
- 虫号: 1176389
28楼2018-08-17 18:39:10
|
油酸钠品牌应该不会太影响，我看到过有人用sigma 82%的都可以。不同品牌CTAB差别比较大，我都是用sigma的，只要之前合成纳米棒没问题就不用换了。球杂质的问题没有完全解决，不过现在少了挺多，你多试几种文献上的不同配比，找到效果比较好的配比。至于你们说的产物中的白色物质我不太清楚，合成产物不应该是偏红棕色吗，怎么会有白色的东西。经验之谈，希望有帮助 发自小木虫Android客户端 |
29楼2018-08-18 23:50:30
★
小木虫: 金币+0.5, 给个红包，谢谢回帖
小木虫: 金币+0.5, 给个红包，谢谢回帖
|
本帖内容被屏蔽 |
30楼2018-08-20 09:59:51
★
小木虫: 金币+0.5, 给个红包，谢谢回帖
小木虫: 金币+0.5, 给个红包，谢谢回帖
|
本帖内容被屏蔽 |
31楼2018-09-29 16:27:26
简单回复
youngen2楼
2018-03-02 17:11
回复
2018-03-02 17:15
回复
光能使者007(金币+1): 谢谢参与
tzynew4楼
2018-03-02 17:27
回复
光能使者007(金币+1): 谢谢参与
2018-03-02 17:36
回复
光能使者007(金币+1): 谢谢参与
2018-03-02 17:53
回复
光能使者007(金币+1): 谢谢参与
nono20097楼
2018-03-02 18:06
回复
光能使者007(金币+1): 谢谢参与
`
rxhmc6888楼
2018-03-02 18:14
回复
光能使者007(金币+1): 谢谢参与
顶
2018-03-02 18:55
回复
光能使者007(金币+1): 谢谢参与
exvgjdq5911楼
2018-03-02 19:33
回复
光能使者007(金币+1): 谢谢参与
垢老3312楼
2018-03-02 20:02
回复
光能使者007(金币+1): 谢谢参与
顶
wdxmu13楼
2018-03-02 20:05
回复
光能使者007(金币+1): 谢谢参与
一 发自小木虫IOS客户端
dqmdvmb6214楼
2018-03-02 20:12
回复
光能使者007(金币+1): 谢谢参与
祝福
kkjbfv2415楼
2018-03-02 20:14
回复
光能使者007(金币+1): 谢谢参与
drjycg11716楼
2018-03-02 21:02
回复
光能使者007(金币+1): 谢谢参与