For TiO2 nanotubes with 22-nm pore diameter and 34-nm wall thickness (Figure 80A), upon 320-400 nm illumination at an intensity of 100 mW/cm2, hydrogen gas was generated at the power-time normalized rate of 960 mmol/h W (24 mL/h W) at an overall conversion efficiency of 6.8% as shown in Figure 80B. The length and diameter of the TiO2 nanotubes could be controlled over a wide range (diameter, 15-120 nm; length, 20 nm to 10 µm) with the applied potential between 1 and 25 V in optimized phosphate/HF electrolytes. They also claimed that, for illumination at 320-400 nm (98 mW/cm2), the TiO2 nanotube-array photoanodes could generate H2 by H2O photoelectrolysis with a photoconversion efficiency of 12.25%。 when doped with carbon, TiO2-xCx nanotube arrays showed more efficient water splitting under UV and visible light illumination (>420 nm) than pure TiO2 nanotube arrays。 请问这几句话怎么翻译  |
回复此楼» 本帖@通知
» 猜你喜欢
0703化学调剂
已经有12人回复
-
0703化学 305求调剂
已经有4人回复
-
0703化学调剂，求各位老师收留
已经有10人回复
-
271材料工程求调剂
已经有5人回复
-
281求调剂（0805）
已经有16人回复
-
304求调剂
已经有6人回复
-
材料工程专硕调剂
已经有6人回复
-
一志愿天大材料与化工（085600）总分338
已经有4人回复
-
085700资源与环境308求调剂
已经有3人回复
-
求材料调剂
已经有8人回复
sqlg888
铁虫 (正式写手)
- SFL-EPI: 1
- 应助: 163 (高中生)
- 金币: 4544.2
- 红花: 27
- 帖子: 995
- 在线: 191.8小时
- 虫号: 4176864
- 注册: 2015-10-27
- 专业: 民族药学
【答案】应助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
感谢参与，应助指数 +1
jina123: 金币+12, ★★★很有帮助 2016-01-07 14:31:04
感谢参与，应助指数 +1
jina123: 金币+12, ★★★很有帮助 2016-01-07 14:31:04
|
在波长320-400nm 、强度100 mW/cm2下照射TiO2纳米管（孔径22nm和壁厚34nm）（如图80A），产生氢气，能量 - 时间归一化速率为960 mmol/h W（24 mL/h W），总光电转换效率为6.8％（如图80B）。 在优化后的磷酸盐/ HF电解液中施加电位1-25 V，二氧化钛纳米管的长度和直径可控制在一定范围内（直径：15-120纳米;长度：20纳米至10微米）。 他们还报道，在波长320-400nm、强度98 mW/cm2照射下，TiO2纳米管阵列的光电阳极能通过光电解水产生氢气，光电转换效率为12.25％。 加入碳的TiO2-XCX纳米管阵列表现出在紫外光和可见光照射下（>420nm）比纯的二氧化钛纳米管阵列有更高的分解水制氢效率。 |
2楼2016-01-07 10:59:06
sqlg888
铁虫 (正式写手)
- SFL-EPI: 1
- 应助: 163 (高中生)
- 金币: 4544.2
- 红花: 27
- 帖子: 995
- 在线: 191.8小时
- 虫号: 4176864
- 注册: 2015-10-27
- 专业: 民族药学
3楼2016-01-07 14:34:31
50