【求助】重复2013年Nanoscale文献合成Fe3O4时，发现柠檬酸钠不溶于二乙二醇，怎么办？ 已有2人参与
|
|
重复文献One-step synthesis of monodisperse, water-soluble ultra-small Fe3O4 nanoparticles for potential bio-application,Nanoscale, 2013, 5, 2133 文献步骤为In a typical synthesis of 3.1 nm Fe3O4 nanoparticles, anhydrous FeCl3 (4 mmol) was first vigorously mixed with 40 mL of DEG to form a clear solution. Then, Na3Cit (1.6 mmol) was added and the mixture was heated at 80 °C with stirring to form a clear solution. After dissolving anhydrous NaOAc (12.0 mmol) in the above solution, the mixture was transferred into a Teflon-lined stainless-steel autoclave (100 mL capacity) and sealed in air. Following this, the autoclave was kept at 200 °C for 6 h. After being allowed to cool naturally to room temperature, the black products were collected by centrifugation (12 000 rpm, 30 min)and washed with ethanol three times. 就是把无水氯化铁溶解于DEG中形成清液，然后加入柠檬酸钠置于80°C中水浴至澄清，最后加入乙酸钠，混合均匀转移至反应釜中200°C反应6h。。。我们实验室没有无水的氯化铁，我就用六水的来试试，结果能溶解，但是柠檬酸钠就溶解不了，80°C搅拌1h都溶解不了，超声过也没变化，加入乙酸钠后，乙酸钠溶解了一部分。。。现在应该怎么办啊？做不好第一步就没法转移进反应釜了都。。。跪求大神帮忙~~~ |
回复此楼» 猜你喜欢
南京晓庄学院绿色能源材料团队招生
已经有0人回复
-
北方工业大学储能技术-02电化学储能与氢能方向招收2026级二次调剂学生
已经有0人回复
-
金属材料论文润色/翻译怎么收费?
已经有51人回复
-
求助WO3.cif文件 对应PDF卡片 43-1035，单斜晶系 , P21/n 。
已经有2人回复
-
稀土发光分析｜核壳结构｜寿命拟合
已经有13人回复
-
稀土发光分析｜核壳结构｜寿命拟合
已经有6人回复
-
稀土发光分析｜核壳结构｜寿命拟合
已经有0人回复
-
稀土发光分析｜核壳结构｜寿命拟合
已经有0人回复
-
26 届青岛大学纺织化学与染整工程硕士（液体纳米分散染料方向）求申博建议
已经有3人回复
-
26 届青岛大学纺织化学与染整工程（液体纳米分散染料）求浙理工纺织 / 材料博导名额
已经有1人回复
» 本主题相关价值贴推荐，对您同样有帮助:
- 【急】求助一下：做金/氧化锌复合材料，表征时紫外可见光谱和IPCE对不上？
已经有0人回复
- 【求助】李亚栋院士angew上的那篇Fe3O4纳米球的合成问题-PEG的溶解！
已经有9人回复
- 【求助必读】文献版求助者必读（2013版)
已经有351人回复
- 【求助】在Gaussview中设置入射光【已搜索无重复】
已经有2人回复
- 英文电子书Polyolefin Foams——【已搜索，无重复】
已经有127人回复
- 外文书籍求助版版规（2011版）
已经有76人回复
- 【求助】求电子版 2010-2013年云南重楼行业投资前景战略研究及企业规划建设指导报告
已经有0人回复
2楼2015-08-14 11:35:18
3楼2015-08-14 14:49:20
4楼2015-08-14 16:02:57
5