| 研究配置不同含水率的NMMO试剂，寻找溶解棉纤维素的最佳含水率；溶液的流变性能；制备纤维素膜时凝固浴温度、溶液的浓度、以及塑化剂甘油对纤维素膜力学性能、结晶性能、官能团组成等的影响。通过实验发现NMMO含水率在13.3%左右，溶解温度在90℃左右时棉纤维素溶解最快；通过溶液流变得到纤维素溶液是切力变稀体；通过纤维素膜力学性能测试发现，凝固浴温度在28℃时纤维素膜的断裂强度和断裂伸长率最高，断裂伸长率随着纤维素溶液浓度的升高而降低，断裂强度随着纤维素溶液浓度升高而升高；制膜时发现有塑化剂甘油作用，得到的纤维素膜表面光滑，在测试时发现纤维素膜有韧性；通过X射线衍射发现制备纤维素膜后纤维素结晶度下降；红外光谱分析后发现，制膜前后纤维素的官能团没有发生变化。 |
回复此楼» 猜你喜欢
售一区SCI文章T0P，我:8O.551.O54,科目全,可十急
已经有9人回复
-
售SCI-T0P文章，我:8O.5.5.1.O.54,科目齐全,可+急
已经有3人回复
-
考博求助
已经有3人回复
-
售SCI一区文章，我:8.O.551.O.5.4,科目全,可伽急
已经有5人回复
-
售SCI一区T0P文章，我:8.O.55.1.O.5.4,科目全,可+急
已经有4人回复
-
售SCI一区T0P文章，我:8.O.55.1.O.5.4,科目全,可+急
已经有5人回复
-
售SCI-T0P文章，我:8O.5.5.1.O.54,科目齐全,可+急
已经有9人回复
-
售一区SCI文章T0P，我:8O.551.O54,科目全,可十急
已经有9人回复
-
售SCI一区T0P文章，我:8.O.55.1.O.5.4,科目全,可+急
已经有10人回复
-
售SCI一区文章，我:8.O.551.O.5.4,科目全,可伽急
已经有6人回复
genhunter
至尊木虫 (著名写手)
- 翻译EPI: 387
- 应助: 259 (大学生)
- 金币: 9757.4
- 散金: 10
- 红花: 60
- 帖子: 2484
- 在线: 1793小时
- 虫号: 2558361
- 注册: 2013-07-22
- 专业: 肿瘤化学药物治疗
【答案】应助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ...
自由的小鸟: 金币+300, 翻译EPI+1, ★★★★★最佳答案 2015-06-12 20:12:16
自由的小鸟: 金币+300, 翻译EPI+1, ★★★★★最佳答案 2015-06-12 20:12:16
| NMMO reagents with different water contents were prepared and studied for the optimum water content to dissolve cotton cellulose; The rheological properties of the solution was determined; Various parameters for the preparation of cellulose membrane by coagulation method, such as bath temperature and cellulose concentration were studied. In addition, the influence of the addition of glycerin as a plasticizer on cellulose membrane mechanical properties, crystallization properties, the composition of functional groups were studied. Through experiments we found that NMMO with a water content at around 13.3%, the temperature at about 90 DEG C had the fastest dissolution rate for cotton cellulose. Rheological studies indicated that the cellulose solution obtained was a shear thinning fluid. Mechanical properties tests on the cellulose membrane showed that cellulose membranes obtained under a coagulation bath temperature at 28 DEG C had the maximal fracture strength and elongation at break. The elongation at break decreased with increasing cellulose concentrations, while the fracture strength increased with increasing cellulose concentrations. Glycerol played a plasticizer role during membrane preparation, cellulose membrane with glycerol had a smooth surface, the tests found that the cellulose membrane prepared with glycerol had tenacity. Using X - ray diffraction method we found that cellulose in membranes had reduced crystallinity; infrared spectrometry analysis revealed that there was no change for the functional groups in cellulose before and after membrane preparation. |
2楼2015-06-12 16:13:25