[求助] 求大神

In order to determine suitable thermal
conditions for the formation of aluminum
titanate (samples “2”), the green bodies
prepared from the Al2O3/TiO2 powder mixture
were heat-treated in air at two different
temperatures (1500 °C and 1650 °C) and
holding times (2 h and 4 h). The crystalline
phase content in the heat-treated samples was
analyzed by X-ray diffraction. Based on the
results, which will be presented in the “Results
and Discussion” section, 1650 °C and 4 h
holding time were chosen for the synthesis of
Al2TiO5.
回复此楼

» 猜你喜欢
1楼 2015-04-21 22:14:01
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

灿灿妹

至尊木虫 (著名写手)

【答案】应助回帖

★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
k86475586: 金币+20, 翻译EPI+1, ★★★很有帮助 2015-04-23 08:42:10
为了确定钛酸铝（样品2）形成的最适热条件，用来制备氧化铝/二氧化钛混合粉末的胚体分别在两个不同的温度下（1500 °C 和 1650 °C）进行热处理，其停留时间分别为2h和4h。
热处理样品中结晶相的含量用X射线衍射来分析。
基于会在"结果与讨论"部分提出的实验结果，选择了温度1650 °C以及4h停留时间作为制备钛酸铝的最佳热条件。
赞一下 回复此楼
执此一生，只为一人，天涯海角，惟愿君安
2楼2015-04-22 08:09:02
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

hool

捐助贵宾 (正式写手)

木星之王

【答案】应助回帖

★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
k86475586: 金币+20, ★★★很有帮助 2015-04-23 08:42:21
为了确定钛酸铝（样品2）形成的适合热条件，我们分别在两个不同的温度下（1500 °C 和 1650 °C）对制备氧化铝/二氧化钛混合粉末的胚体进行热处理，停留时间分别为2小时和4小时。
并利用X射线衍射来分析热处理样品中晶相的含量。
根据在"结果与讨论"部分给出的实验结果，我们选择温度1650 °C以及4小时停留时间作为制备钛酸铝的条件。
赞一下 回复此楼
3楼2015-04-22 09:52:15
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

k86475586

铜虫 (小有名气)
引用回帖:
2楼: Originally posted by 灿灿妹 at 2015-04-22 08:09:02
为了确定钛酸铝（样品2）形成的最适热条件，用来制备氧化铝/二氧化钛混合粉末的胚体分别在两个不同的温度下（1500 °C 和 1650 °C）进行热处理，其停留时间分别为2h和4h。
热处理样品中结晶相的含量用X射线衍射来 ...

大神我还有一段你帮忙翻译了吧
赞一下 回复此楼
4楼2015-04-23 08:48:58
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
相关版块跳转 我要订阅楼主 k86475586 的主题更新
41/1返回列表
普通表情 龙 兔 虎 猫
最具人气热帖推荐 [查看全部] 作者 回/看 最后发表
[公派出国] 售SCI一区文章，我:8.O.551.O.5.4,科目全,可伽急 +4 G2rhSvqvhNzl 2026-11-10 5/250 2026-11-13 11:37 by Equinoxhua
[硕博家园] 售SCI一区T0P文章，我:8.O.55.1.O.5.4,科目全,可+急 +6 FChKX8meu1ds 2026-11-09 10/500 2026-11-13 11:08 by Equinoxhua
[硕博家园] 售SCI一区T0P文章，我:8O.55.1.O.54,科目全,可伽急 +5 C6CRn66RYYXS 2026-11-10 9/450 2026-11-13 11:02 by Equinoxhua
[考博] 27博士 +5 锦鲤送福至 2026-11-10 5/250 2026-11-13 06:22 by wlf1982
[论文投稿] 售SCI一区T0P文章，我:8.O.55.1.O54,科目全,可伽急 +3 TgvkbZZl9tqB 2026-11-11 4/200 2026-11-12 12:51 by ECLTXnJnRSXf
[硕博家园] 售SCI一区文章，我:8.O.551.O.5.4,科目全,可伽急 +3 TgvkbZZl9tqB 2026-11-11 4/200 2026-11-12 12:28 by ECLTXnJnRSXf
[教师之家] 售SCI一区文章，我:8.O.551.O.5.4,科目全,可伽急 +4 Z7qfCsdIiD1T 2026-11-10 9/450 2026-11-12 11:22 by HajghKOMynmz
[硕博家园] 售SCI-T0P文章，我:8O.5.5.1.O.54,科目齐全,可+急 +5 Z7qfCsdIiD1T 2026-11-10 8/400 2026-11-12 11:20 by HajghKOMynmz
[基金申请] 售SCI文章，我:8O5.5.1.O.54,科目齐全,可+急 +5 czAiolzR0IJC 2026-11-10 9/450 2026-11-12 11:11 by HajghKOMynmz
[考博] 售SCI一区T0P文章，我:8.O.55.1.O.54,科目齐全,可+急 +3 G2rhSvqvhNzl 2026-11-10 5/250 2026-11-12 10:49 by HajghKOMynmz
[教师之家] 售SCI一区T0P文章，我:8O.55.1.O.5.4,科目齐全,可+急 +3 C6CRn66RYYXS 2026-11-10 8/400 2026-11-12 10:16 by HajghKOMynmz
[基金申请] 售SCI一区T0P文章，我:8.O.55.1.O.54,科目齐全,可+急 +6 zSbvVX9JFl9J 2026-11-09 9/450 2026-11-12 09:21 by HajghKOMynmz
[考研] 售SCI一区T0P文章，我:8.O.55.1.O.54,科目齐全,可+急 +5 czAiolzR0IJC 2026-11-10 5/250 2026-11-12 06:25 by 9fOTqj074tIg
[硕博家园] 售SCI文章，我:8O5.5.1.O.54,科目齐全,可+急 +3 G2rhSvqvhNzl 2026-11-10 5/250 2026-11-12 06:14 by 9fOTqj074tIg
[硕博家园] 售SCI一区T0P文章，我:8.O.55.1.O.5.4,科目全,可+急 +3 C6CRn66RYYXS 2026-11-10 5/250 2026-11-12 06:03 by 9fOTqj074tIg
[教师之家] 售SCI文章，我:8O5.5.1.O.54,科目齐全,可+急 +4 C6CRn66RYYXS 2026-11-10 4/200 2026-11-12 06:03 by 9fOTqj074tIg
[考博] 售SCI一区T0P文章，我:8.O.55.1.O.54,科目齐全,可+急 +3 FChKX8meu1ds 2026-11-09 8/400 2026-11-12 05:30 by 9fOTqj074tIg
[基金申请] 售SCI一区T0P文章，我:8.O.55.1.O.54,科目齐全,可+急 +5 FChKX8meu1ds 2026-11-09 7/350 2026-11-12 05:30 by 9fOTqj074tIg
[教师之家] 售SCI一区文章，我:8.O.55.1.O.54,科目齐全,可伽急 +6 0TEMgxdT1eIw 2026-11-09 8/400 2026-11-12 05:00 by 9fOTqj074tIg
[考博] 申请环境，微生物方向博士 +3 浅笑09 2026-11-08 3/150 2026-11-10 12:44 by 可淡不可忘
信息提示
关闭
请填处理意见
关闭