小木虫论坛-学术科研互动平台 » 化学化工区 » 催化 » 催化剂制备 » 纳米四氧化三铁负载金属镍问题
51/1返回列表
查看: 2157  |  回复: 11
只看楼主 @他人 存档 新回复提醒 (忽略) 收藏    在APP中查看
当前只显示满足指定条件的回帖，点击这里查看本话题的所有回帖

小鱼和小透

新虫 (初入文坛)

[求助] 纳米四氧化三铁负载金属镍问题 已有2人参与

Ferrite magnetic nanoparticles
Fe3O4 (2 g) and NiCl2·6H2O (10 wt% of nickel on ferrite) were stirred at
room temperature in aqueous solution for 1 h. After impregnation, the
suspension was adjusted to pH 12 by adding sodium hydroxide (0.5m)
and stirred for 10 to 12 h. The solid was washed by distilled water (5
10 mL). The obtained metal precursors were reduced by adding an aqueous
solution of 0.2m NaBH4 dropwise under gentle stirring in an ice–
water bath for 30 min until no bubbles were observed in the solution.
The resulting Fe3O4Ni MNPs were ultrasonicated for 10 min and then
washed with distilled water and subsequently with ethanol. The synthesized
Fe3O4Ni MNPs were characterized by several techniques such as
XRD, ICP-AES, TEM, and FEG-SEM-EDS.，请问这里面的硼氢化钠应该怎么处理？我直接配制的硼氢化钠溶液加到溶液中去，没有得到理想效果。

[ Last edited by liwentao2010 on 2015-3-18 at 18:37 ]
回复此楼

» 收录本帖的淘帖专辑推荐

四氧化三铁纳米颗粒制备、修饰及包覆

» 猜你喜欢

» 本主题相关商家推荐: (我也要在这里推广)

» 本主题相关价值贴推荐，对您同样有帮助:
1楼 2014-07-04 11:04:07
已阅   关注TA 给TA发消息 送TA红花 TA的回帖

changlinqu

金虫 (正式写手)
试一下溶于冰水…或者在冰水浴条件下溶解

[ 发自小木虫客户端 ]
赞一下(1人) 回复此楼
Thinkbig,startsmall,andactquickly!
8楼2014-07-05 17:23:58
已阅   关注TA 给TA发消息 送TA红花 TA的回帖
查看全部 12 个回答

liwentao2010

荣誉版主 (文坛精英)

山涛

优秀版主优秀版主优秀版主优秀版主优秀版主

【答案】应助回帖

感谢参与，应助指数 +1
方法没有什么问题，正常。不知道楼主所说效果不理想，是催化效果不好？
赞一下 回复此楼
加油！
2楼2014-07-04 12:30:45
已阅   关注TA 给TA发消息 送TA红花 TA的回帖

小鱼和小透

新虫 (初入文坛)
引用回帖:
2楼: Originally posted by liwentao2010 at 2014-07-04 12:30:45
方法没有什么问题，正常。不知道楼主所说效果不理想，是催化效果不好？

感觉是硼氢化钠配置问题，请问怎么配制0.2M NaBH4水溶液
赞一下 回复此楼
3楼2014-07-04 14:18:56
已阅   关注TA 给TA发消息 送TA红花 TA的回帖

liwentao2010

荣誉版主 (文坛精英)

山涛

优秀版主优秀版主优秀版主优秀版主优秀版主
引用回帖:
3楼: Originally posted by 小鱼和小透 at 2014-07-04 14:18:56
感觉是硼氢化钠配置问题，请问怎么配制0.2M NaBH4水溶液...

称取一定质量NaBH4溶于水。
赞一下 回复此楼
加油！
4楼2014-07-04 19:38:11
已阅   关注TA 给TA发消息 送TA红花 TA的回帖
查看全部 12 个回答
最具人气热帖推荐 [查看全部] 作者 回/看 最后发表
[考研] 286求调剂 +10 Faune 2026-03-21 10/500 2026-03-21 23:34 by 314126402
[考研] 广西大学材料导师推荐 +3 夏夏夏小正 2026-03-17 5/250 2026-03-21 22:20 by 金昊ML
[考研] 求调剂 +5 十三加油 2026-03-21 5/250 2026-03-21 18:48 by 学员8dgXkO
[考研] 一志愿重庆大学085700资源与环境总分308求调剂 +7 墨墨漠 2026-03-20 7/350 2026-03-21 16:36 by barlinike
[考研] 08工科 320总分 求调剂 +6 梨花珞晚风 2026-03-17 6/300 2026-03-21 03:40 by JourneyLucky
[考研] 初始318分求调剂（有工作经验） +3 1911236844 2026-03-17 3/150 2026-03-21 02:33 by JourneyLucky
[考研] 化学求调剂 +4 临泽境llllll 2026-03-17 5/250 2026-03-21 02:23 by JourneyLucky
[考研] 华东师范大学-071000生物学-293分-求调剂 +3 研究生何瑶明 2026-03-18 3/150 2026-03-21 01:30 by JourneyLucky
[考研] 材料专硕英一数二306 +7 z1z2z3879 2026-03-18 7/350 2026-03-20 23:48 by JourneyLucky
[考研] 一志愿中海洋材料工程专硕330分求调剂 +8 小材化本科 2026-03-18 8/400 2026-03-20 23:16 by JourneyLucky
[考研] 一志愿南京理工大学085701资源与环境302分求调剂 +4 葵梓卫队 2026-03-18 6/300 2026-03-20 23:02 by JourneyLucky
[考研] 一志愿吉林大学材料学硕321求调剂 +11 Ymlll 2026-03-18 15/750 2026-03-20 19:40 by 丁丁*
[考研] 求调剂 +3 @taotao 2026-03-20 3/150 2026-03-20 19:35 by JourneyLucky
[考研] 材料与化工求调剂 +7 为学666 2026-03-16 7/350 2026-03-19 14:48 by 尽舜尧1
[考研] 0703化学调剂 +5 pupcoco 2026-03-17 8/400 2026-03-19 13:58 by houyaoxu
[考研] 材料考研调剂 +3 xwt。 2026-03-19 3/150 2026-03-19 11:22 by w沐阳w
[考研] 材料，纺织，生物（0856、0710），化学招生啦 +3 Eember. 2026-03-17 9/450 2026-03-18 10:28 by Eember.
[考研] 293求调剂 +11 zjl的号 2026-03-16 16/800 2026-03-18 08:10 by zhukairuo
[考博] 26申博 +4 八6八68 2026-03-16 4/200 2026-03-17 13:00 by 轻松不少随
[考研] 0856求调剂 +3 刘梦微 2026-03-15 3/150 2026-03-16 10:00 by houyaoxu
信息提示
关闭
请填处理意见
关闭