The novel magnetic nanocomposites with the special stoichiometries of Ba0.34Sr0.34Cd0.16Zn0.16Fe12O19 (S1) and Ba0.69Sr0.17Cd0.07Zn0.07Fe12O19 (S2) were successfully synthesized by the self-assembly reflux procedure. EDTA was used as a complexing agent to prepare these magnetic ferrite nanoparticles with a uniform morphology. The excellent crystallinity of the samples was provided via the calcination planning at 450 and 850 C for 2 h. The prepared ferrite nanocomposites indicated the high saturation magnetization of 66.59 and 65.09 emu/g. In addition, the resulting products revealed excellent microwave absorbing properties at the frequency range of 8–12 GHz. The maximum reflection losses of 25 and 35 dB were measured for samples (S1) and (S2) after calcination at 850 C with an optimum thickness of 2.1 mm,respectively. The results showed that the increase of calcination temperature to 850 C improves the microwave absorbing properties of the prepared absorbers. These results can be due to establishment of the crystallinity of ferrite structure and arrangement of the particles in nanoscale with the average sizes of 43 and 38 nm, respectively. Therefore, these synthesized ferrite composites can be applied as a microwave absorber for EMI shielding. |
回复此楼» 猜你喜欢
同年申请2项不同项目，第1个项目里不写第2个项目的信息，可以吗
已经有8人回复
-
依托企业入选了国家启明计划青年人才。有无高校可以引进的。
已经有7人回复
-
依托企业入选了国家启明计划青年人才。有无高校可以引进的。
已经有10人回复
-
天津大学招2026.09的博士生，欢迎大家推荐交流（博导是本人）
已经有9人回复
-
有院领导为了换新车，用横向课题经费买了俩车
已经有10人回复
-
AI 太可怕了，写基金时，提出想法，直接生成的文字比自己想得深远，还有科学性
已经有6人回复
-
酰胺脱乙酰基
已经有13人回复
-
有时候真觉得大城市人没有县城人甚至个体户幸福
已经有10人回复
blacklight
木虫 (著名写手)
- 翻译EPI: 2
- 应助: 45 (小学生)
- 金币: 1806.7
- 散金: 5494
- 红花: 15
- 帖子: 1327
- 在线: 558.8小时
- 虫号: 848969
- 注册: 2009-09-16
- 性别: GG
- 专业: 污染控制化学
【答案】应助回帖
|
通过回流自组装的方法，具有特别化学计量数的Ba0.34Sr0.34Cd0.16Zn0.16Fe12O19 (S1)和Ba0.69Sr0.17Cd0.07Zn0.07Fe12O19 (S2)两种新颖磁性复合物被合成出来。EDTA作为络合剂被用来制备具有均匀形貌的铁酸盐磁性纳米粒子。通过在450度和850度煅烧两个小时，我们获得了具有非常高结晶度的样品。 制备的铁酸盐纳米复合物的饱和磁化率高达66.59 和 65.09 emu/g。此外，终产物对频率在8–12 GHz的微波具有非常吸收性能，对于测试的S1和S2两个样品来说，他们的最大反射损耗为25 和35 dB 。 （after calcination at 850 C with an optimum thickness of 2.1 mm,respectively，这句话有问题，我尝试翻译）经过850度的煅烧后，材料的优化厚度为2.1毫米。结果显示，当煅烧温度升高到850度后，我们制备的吸波材料的微波吸收性能提高了，这可以归因于铁酸盐结晶结构的形成和粒子在43纳米和38纳米这个纳米尺度的重新排列。因此，合成的铁酸盐复合物可以被用作微波吸收剂来进行抗电磁干扰。 楼主不要忘记金币啊  |
2楼2014-06-18 09:22:52
blacklight
木虫 (著名写手)
- 翻译EPI: 2
- 应助: 45 (小学生)
- 金币: 1806.7
- 散金: 5494
- 红花: 15
- 帖子: 1327
- 在线: 558.8小时
- 虫号: 848969
- 注册: 2009-09-16
- 性别: GG
- 专业: 污染控制化学
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
RXMCDM: 金币+1, 多谢应助！ 2014-06-18 20:47:16
wanghaiju(RXMCDM代发): 金币+29, 多谢应助！ 2014-07-05 09:28:54
RXMCDM: 金币+1, 多谢应助！ 2014-06-18 20:47:16
wanghaiju(RXMCDM代发): 金币+29, 多谢应助！ 2014-07-05 09:28:54
|
通过回流自组装的方法，具有特别化学计量数的Ba0.34Sr0.34Cd0.16Zn0.16Fe12O19 (S1)和Ba0.69Sr0.17Cd0.07Zn0.07Fe12O19 (S2)两种新颖磁性复合物被合成出来。EDTA作为络合剂被用来制备具有均匀形貌的铁酸盐磁性纳米粒子。通过在450度和850度煅烧两个小时，我们获得了具有非常高结晶度的样品。 制备的铁酸盐纳米复合物的饱和磁化率高达66.59 和 65.09 emu/g。此外，终产物对频率在8–12 GHz的微波具有非常吸收性能，对于测试的S1和S2两个样品来说，他们的最大反射损耗为25 和35 dB 。 （after calcination at 850 C with an optimum thickness of 2.1 mm,respectively，这句话有问题，我尝试翻译）经过850度的煅烧后，材料的优化厚度为2.1毫米。结果显示，当煅烧温度升高到850度后，我们制备的吸波材料的微波吸收性能提高了，这可以归因于铁酸盐结晶结构的形成和粒子在43纳米和38纳米这个纳米尺度的重新排列。因此，合成的铁酸盐复合物可以被用作微波吸收剂来进行抗电磁干扰。 楼主不要忘记金币啊 |
3楼2014-06-18 12:48:21