[求助] 沉淀浸渍法

沉淀浸渍法的英文怎么说？相关文献可以给两个看看不求教了！

回复此楼

» 猜你喜欢

1楼 2013-07-03 12:59:31

已阅回复此楼关注TA 给TA发消息送TA红花 TA的回帖

342951000

银虫 (小有名气)

应助: 0 (幼儿园)
金币: 1068.9
散金: 14
红花: 5
帖子: 187
在线: 63.3小时
虫号: 1483774
注册: 2011-11-09
专业: 有机合成

引用回帖:

2楼: Originally posted by zyhou at 2013-07-03 13:29:24
很少有人这么称呼，把你的步骤列出来看看如何定义！
有“沉淀沉积”法：precipitation，An aqueous solution containing 0.01 g/mL H2PtCl6 was added dropwise to a stirred suspension of 2.0 g support (HNO3-M ...

汉文的有许多叫共沉淀-浸渍法！主要就是用酸或碱把浸渍液中和，生产沉淀，搅拌均匀，滴加到载体上浸渍。不知道这是不是应该叫沉淀浸渍法！

赞一下

回复此楼

3楼2013-07-04 08:53:18

已阅回复此楼关注TA 给TA发消息送TA红花 TA的回帖

查看全部 7 个回答

zyhou

专家顾问 (文坛精英)

专家经验: +3748
C-EPI: 74
应助: 4970 (副教授)
贵宾: 2.947
金币: 39203.7
散金: 14624
红花: 415
帖子: 10637
在线: 2545.8小时
虫号: 373328
注册: 2007-05-16
性别: GG
专业: 催化化学
管辖: 催化

【答案】应助回帖

★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
感谢参与，应助指数 +1
非文王木木: 金币+5, 感谢应助··· 2013-07-03 15:09:37
342951000: 金币+8, ★有帮助 2013-07-04 08:53:35
342951000: 金币+8, ★有帮助 2013-07-15 11:36:52
342951000: 金币+4 2013-09-24 17:55:36

很少有人这么称呼，把你的步骤列出来看看如何定义！
有“沉淀沉积”法：precipitation，An aqueous solution containing 0.01 g/mL H2PtCl6 was added dropwise to a stirred suspension of 2.0 g support (HNO3-MWNTs, H2O2-MWNTs and S-MWNTs). The slurry was stirred for 30 min at room temperature and sonicated for 2 h, reduced by an aqueous solution of KBH4. And then the catalyst was filtered and washed with distilled deionized water to remove residual chlorine. The loading amount of Pt was controlled and confirmed by ICP as 5.0 wt.% of the support.
文献：Applied Catalysis B: Environmental, Volume 106, Issues 3–4, 11 August 2011, Pages 423-432

有“直接浸渍”法：Ni catalysts sized from 4.5 to 45.0 nm were prepared via direct impregnation of [Ni(en)3]2+ (en, ethylenediamine), [Ni(EDTA)]2− (EDTA; ethylenediaminetetraacetic acid), nickel(II) acetylacetonate dihydrate (99+%), nickel(II) acetate, and Ni(NO3)2⋅6H2O onto a spherical SiO2 support。
Journal of Catalysis, Volume 250, Issue 2, 10 September 2007, Pages 331-341

有“共沉淀”法：A series of Cu0.4Zn5.6−xMgxAl2(OH)16CO3 LDHs were prepared by co-precipitation. Cu(NO3)2·3H2O (0.01 mol), Al(NO3)3·9H2O (0.05 mol), Zn(NO3)2·6H2O, and Mg(NO3)2·6H2O (AR, Sinopharm Chemical Reagent Co. Ltd., China) were dissolved together in 400 mL deionized water. The total amount of Zn(NO3)2·6H2O and Mg(NO3)2·6H2O was controlled to 0.14 mol, and this mixed solution is referred to as A. Solution B was a mixture of Na2CO3 and NaOH (AR, Sinopharm Chemical Reagent Co. Ltd., China) with concentrations of 0.25 and 0.8 mol/L, respectively. Solutions A and B were simultaneously added into a glass reactor under vigorous stirring at room temperature and of a pH value of 9.5. The slurry was transferred into a custom-designed stainless autoclave (1000 mL) equipped with a Teflon inner layer, put into an oil bath, and aged at 120 °C for 20 h under stirring, filtered off, and washed thoroughly with distilled water. The precipitate was then dried overnight at 80 °C and identified as Cu0.4Zn5.6−xMgxAl2(OH)16CO3, in which x refers to the amount of Mg (0 < x < 5.6).
参考文献：Journal of Catalysis, Volume 296, December 2012, Pages 1-11