lily1988815金虫 (小有名气)
|
[求助]
按照文献，为什么制备不出一样的催化剂
|
|
|
《b-MnO2 nanowires: A novel ozonation catalyst for water treatment》 制备方法 Ozone was generated in a laboratory ozone generator from pure oxygen, and the flow rate of ozone was 0.30 mg/min. In a typical procedure for the synthesis of b-MnO2 nanowires, 2.5 mL of 50 wt.% Mn(NO3)2 solution was diluted to 25.0 mL, and ozone was fed into the bottom of the solution for 30 min under vigorous stirring. With the indraught of ozone, black solid appeared gradually and the clear solution turned into black slurry finally. Then the suspension was transferred into an autoclave of 48.0 mL, sealed and maintained at 200 °Cfor 8h. After this, the autoclave was cooled to room temperature naturally. The resulting solid products were washed with water, and dried at 120 °C for 8 h. The obtained products were collected for the following characterization. 我按照文献的方法制备，可是为什么总是制备不出来，请高手指点，谢谢 |
回复此楼» 猜你喜欢
求问：LATP煅烧应该使用什么容器？
已经有0人回复
-
西安交通大学 赵旭课题组 招收研究助理--电催化方向
已经有1人回复
-
物理化学论文润色/翻译怎么收费?
已经有181人回复
-
西安交通大学 赵旭课题组 2026年招收博士后-电催化方向
已经有0人回复
-
焙烧后的拉西环状铁钼催化剂侧面硬度高，应该如何降低？
已经有1人回复
-
欢迎来稿
已经有212人回复
-
双一流大学湘潭大学“化工过程模拟与强化”国家地方联合工程研究中心招收博士生
已经有52人回复
-
大连海事大学国家级人才团队（船舶洁净能源研究中心）2027年博士研究生招生启事
已经有1人回复
lily1988815
金虫 (小有名气)
- 应助: 0 (幼儿园)
- 金币: 2244.8
- 红花: 1
- 帖子: 124
- 在线: 55小时
- 虫号: 1641443
- 注册: 2012-02-25
- 专业: 聚合物共混与复合材料
18楼2013-01-05 17:46:40
2楼2013-01-04 09:59:14
xiaodoudou
木虫 (小有名气)
- 应助: 25 (小学生)
- 金币: 2139.7
- 红花: 5
- 帖子: 135
- 在线: 87.2小时
- 虫号: 446268
- 注册: 2007-10-29
- 性别: MM
- 专业: 催化化学
3楼2013-01-04 11:09:59
王晓萌
木虫 (著名写手)
- 应助: 175 (高中生)
- 贵宾: 0.462
- 金币: 2664.6
- 散金: 7615
- 红花: 64
- 沙发: 1
- 帖子: 2096
- 在线: 221.9小时
- 虫号: 1262624
- 注册: 2011-04-12
- 性别: MM
- 专业: 金属有机化学
4楼2013-01-04 12:26:53