[交流] 氧化锌作用再探讨

之前发过一个帖子询问了氧化锌在玻璃组分中的作用,在之后的检索中,发现了氧化锌的一些新用途.本人是研究浮法玻璃的新人小菜鸟,以下一段内容摘自PPG1988的一篇专利,针对里面氧化锌的反应部分,我不是特别明白,希望有达人能给予指点.
Furhtermore, it is taught that in glass in which sulfur is present as a refining aid, as would be the case with most commercially produced flat glass, substantial amounts of zinc oxide should be included to prevent the formation of amber coloration when reducing conditions are imposed. But glass containing zinc oxide has been found to be incompatible with the float process, by which most flat glass is produced.This is due to the volatility of zinc oxide in the float forming chamber,which not only contaminates the interior of the chamber, but also leads to amber streaks in the glass where the zinc oxide content has been depleted.
这段大约的意思是,玻璃中的澄清剂产生的硫会使玻璃着上琥珀色,而氧化锌常被用于漂白硫产生的琥珀色,但在玻璃成型室中氧化锌很容易挥发,最终导致玻璃上留下琥珀色的条纹.
我的问题集中在,澄清剂分解产生能使玻璃着琥珀色硫化物的反应是
Na2SO4(芒硝)+C(炭粉)=Na2S+2CO2,其中硫化钠是琥珀色的来源.
而之后ZnO如何与Na2S反应产生漂白作用呢?之后的产物又是如何在高温下分解的呢?
谢谢.另外求推荐有没有介绍高温下化学反应的资料推荐?
回复此楼

» 猜你喜欢

» 本主题相关价值贴推荐，对您同样有帮助:

» 抢金币啦！回帖就可以得到:

查看全部散金贴
1楼 2012-11-08 16:16:23
已阅   关注TA 给TA发消息 送TA红花 TA的回帖

flash6669

木虫 (著名写手)
★
小木虫: 金币+0.5, 给个红包，谢谢回帖
进来学习的，可能有这样的作用吧，玻璃学的一直是很有意思的东西
赞一下 回复此楼
2楼2012-11-08 20:40:29
已阅   关注TA 给TA发消息 送TA红花 TA的回帖

米饭团

木虫 (小有名气)
都没人知道么
回复此楼
4楼2012-11-14 13:02:52
已阅   关注TA 给TA发消息 送TA红花 TA的回帖

lupglass

银虫 (小有名气)
★ ★ ★ ★ ★ ★
小木虫: 金币+0.5, 给个红包，谢谢回帖
tjcdp: 金币+5, 代楼主奖励金币 2013-01-21 08:19:01
1、氧化锌在玻璃中的作用是降低熔点。
2、氧化锌本身不会给玻璃着色，应该不是脱色的作用，要脱色使用的互补色，属于物理脱色。
3、氧化锌也不容易挥发，有条纹是因为在实验室熔化玻璃没有搅拌，成分的不均匀造成的。
赞一下 回复此楼
5楼2013-01-21 00:05:53