小木虫论坛-学术科研互动平台 » 化学化工区 » 电化学 » 电化基础 » 镁合金电化学测试的几个问题（制样、腐蚀对结果影响、拟合）
424/5返回列表上一页12345下一页
查看: 3157  |  回复: 41
只看楼主@他人 存档 新回复提醒 (忽略) 收藏    在APP中查看

shamrocksu

铁杆木虫 (著名写手)
引用回帖:
30楼: Originally posted by Jackcd12 at 2013-08-07 15:47:00
这种相关性就不清楚了。

好吧，很多文献也只是把数值列出来，并没有分析多少。。仍然感谢。
赞一下 回复此楼
①好好活着,因为我们要死很久很久…②青春就像卷卫生纸，看着挺多，用着用着就不够了…...
31楼2013-08-07 15:54:14
 已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

shamrocksu

铁杆木虫 (著名写手)
引用回帖:
30楼: Originally posted by Jackcd12 at 2013-08-07 15:47:00
这种相关性就不清楚了。

最近俺一个文章有一条关于极化曲线极化电阻Rp的意见，麻烦您有空看一下，The authors should state clearly how Rp was determined. It is not appropriate to use the Stern Geary equation and icorr determined from Tafel extrapolation with the b values. If that was how Rp was determined, the values and all discussion about it should be deleted. It is ok to analyze the region near the OCP as if it were a linear polarization experiment and take the slope as Rp.我是直接用potentiodynamic做的，Rp值是从c-view得到的，这样求解到底是不是适用？我直接这么说行吗？
赞一下 回复此楼
①好好活着,因为我们要死很久很久…②青春就像卷卫生纸，看着挺多，用着用着就不够了…...
32楼2013-09-01 22:51:35
 已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

Jackcd12

至尊木虫 (知名作家)
只有在弱极化/线性极化（30mV)区域内才可以利用极化曲线求极化电阻。
赞一下 回复此楼
Themoreamanlearns,themoreheknowshisignorance!
33楼2013-09-02 10:43:32
 已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

shamrocksu

铁杆木虫 (著名写手)
引用回帖:
33楼: Originally posted by Jackcd12 at 2013-09-02 10:43:32
只有在弱极化/线性极化（30mV)区域内才可以利用极化曲线求极化电阻。

哦，那就应该对了，谢谢你！
赞一下 回复此楼
①好好活着,因为我们要死很久很久…②青春就像卷卫生纸，看着挺多，用着用着就不够了…...
34楼2013-09-02 11:05:54
 已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

shamrocksu

铁杆木虫 (著名写手)
引用回帖:
33楼: Originally posted by Jackcd12 at 2013-09-02 10:43:32
只有在弱极化/线性极化（30mV)区域内才可以利用极化曲线求极化电阻。

你好，关于Z-simp-win软件拟合的Q的单位是啥？ohm^-1 cm^-2 s^n？有个审稿意见提出这个问题，请教哈。详细意见我发到一个帖子上了，您看看：http://muchong.com/bbs/viewthread.php?tid=6350384
赞一下 回复此楼
①好好活着,因为我们要死很久很久…②青春就像卷卫生纸，看着挺多，用着用着就不够了…...
35楼2013-09-11 21:10:23
 已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

Jackcd12

至尊木虫 (知名作家)
Q的单位就是ohm^-1 cm^-2 s^n
赞一下(1人) 回复此楼
Themoreamanlearns,themoreheknowshisignorance!
36楼2013-09-11 21:45:26
 已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

shamrocksu

铁杆木虫 (著名写手)
引用回帖:
36楼: Originally posted by Jackcd12 at 2013-09-11 21:45:26
Q的单位就是ohm^-1 cm^-2 s^n

您看看这个审稿人的话，我没明白是想让我把C值求出来还是把单位改正就行: 谢谢了
The units you show below are correct for CPE admittance. However, I have two comments. First, it is more common to report CPE magnitude, which would be the inverse of the admittance value. Second, it is strange in the jpg image you sent me that the units shown for Y0 have sec^0.5 rather than sec^n. I have never used ZSimp Win so I can't help you. You should contact the company to ask them about this. The exponent in the unit should be n.

As I mentioned, you can report the two values describing the CPE fit or convert to C in F/cm2, but you cannot simply replace the units of the CPE magnitude with F/cm2.

I hope this helps. Please clarify the situation with the software company.
赞一下 回复此楼
①好好活着,因为我们要死很久很久…②青春就像卷卫生纸，看着挺多，用着用着就不够了…...
37楼2013-09-11 22:35:16
 已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

shamrocksu

铁杆木虫 (著名写手)
引用回帖:
36楼: Originally posted by Jackcd12 at 2013-09-11 21:45:26
Q的单位就是ohm^-1 cm^-2 s^n

附件是软件拟合的单位怎么是S-sec^n/cm2, S是指的ohm^-1?
镁合金电化学测试的几个问题（制样、腐蚀对结果影响、拟合）
CPE -2.JPG
赞一下 回复此楼
①好好活着,因为我们要死很久很久…②青春就像卷卫生纸，看着挺多，用着用着就不够了…...
38楼2013-09-12 13:14:16
 已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

Jackcd12

至尊木虫 (知名作家)
引用回帖:
37楼: Originally posted by shamrocksu at 2013-09-11 22:35:16
您看看这个审稿人的话，我没明白是想让我把C值求出来还是把单位改正就行: 谢谢了
The units you show below are correct for CPE admittance. However, I have two comments. First, it is more common  ...

审稿人的意思是要求列出CEP系数大小1/Yo，你写的单位是正确的，Q的单位主要以：S^n/Ohm.cm^2.你拟合后的n=0.5?，他认为直接写成S^n/ohm.cm^2就行了。
另外，用F/cm2并不能简单代表Q的系数，他说的是对的，将Yo转换成C没有统一的公式，曾有人提出过经验式，但采用的人不多，因此，一般不将Q变成电容单位来解释，直接比较Yo或其倒数的大小和n的大小就可以了。
赞一下 回复此楼
Themoreamanlearns,themoreheknowshisignorance!
39楼2013-09-12 20:58:54
 已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

shamrocksu

铁杆木虫 (著名写手)
引用回帖:
39楼: Originally posted by Jackcd12 at 2013-09-12 20:58:54
审稿人的意思是要求列出CEP系数大小1/Yo，你写的单位是正确的，Q的单位主要以：S^n/Ohm.cm^2.你拟合后的n=0.5?，他认为直接写成S^n/ohm.cm^2就行了。
另外，用F/cm2并不能简单代表Q的系数，他说的是对的，将Yo转换 ...

谢谢你，哈哈，总是麻烦你。。。

[ 发自小木虫客户端 ]
赞一下 回复此楼
①好好活着,因为我们要死很久很久…②青春就像卷卫生纸，看着挺多，用着用着就不够了…...
40楼2013-09-13 13:05:35
 已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖