[求助] 关于氧化石墨烯还原后处理的问题... 已有2人参与

将氧化石墨烯(GO)还原后再应该在么处理?怎么干燥?我看文献上许多都说离心水洗,试过离心,转速10000rpm,感觉离心不了,石墨烯还是均匀分散在水中。可不可以直接过滤干燥呀?
回复此楼

» 猜你喜欢

» 本主题相关商家推荐: (我也要在这里推广)

» 本主题相关价值贴推荐,对您同样有帮助:

路漫漫!
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

baiwanqiao

木虫 (正式写手)

好像可以啊,这是我看到的一篇文献:Preparation of a batch of a colloidal suspension of reduced graphene oxide
Graphite oxide (GO) was synthesized from natural graphite(SP-1, Bay Carbon, MI) by the modified Hummers method.
A colloidal suspension of graphene oxide platelets in puri-fied water (50 mg of GO, 3 mg/ml) was prepared in a 250 ml
flask with 2 h of bath ultrasound (VWR B2500A-MT). A sus-pension of graphene oxide in the H2O/N,N -dimethylformam-ide (DMF) solvent mixture was obtained by addition of DMF(volume ratio of DMF:H2O = 9:1) into the aqueous grapheneoxide suspensions. Hydrazine monohydrate (1 l l per 3 mg ofGO) (98%, Aldrich) was subsequently added to the suspension.
Additional stirring with a Teflon-coated stirring bar at 80℃  for 12 h yielded a black suspension of reduced graphene oxide platelets.
路漫漫!
7楼2012-10-22 13:13:17
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
查看全部 13 个回答

jin121

木虫 (正式写手)

【答案】应助回帖

感谢参与,应助指数 +1
你应该把你还原GO的方法贴出来,让大家帮你分析一下,这样直接问,让别人很难回答,因为不同的还原方法,后处理都不一样
NeverGiveUp
2楼2012-09-12 13:02:27
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

baiwanqiao

木虫 (正式写手)

还原方法:将200mg的氧化石墨烯分散于150mg水中,超声1h,再将NaBH4还原剂300g加入到分散液中搅拌半小时,将混合物加热到130℃,反应5小时,使GO完全转化成石墨烯,接下来该怎么处理还原后的石墨烯呢?
路漫漫!
3楼2012-09-12 14:45:57
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

olea

专家顾问 (著名写手)

【答案】应助回帖

感谢参与,应助指数 +1
转速可能低了点,lz做得多的话可以过滤,会损失一些
4楼2012-09-12 15:05:23
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
最具人气热帖推荐 [查看全部] 作者 回/看 最后发表
[考研] 284求调剂 +8 天下熯 2026-02-28 8/400 2026-03-02 00:15 by 暮雨星晴
[基金申请] 本子写完了,给DS兄弟看了,得了92分 +3 Doma 2026-03-01 7/350 2026-03-02 00:00 by jnzsy
[考研] 求调剂 +5 yunziaaaaa 2026-03-01 6/300 2026-03-01 23:57 by ccp273206157
[考研] 一志愿郑大材料学硕298分,求调剂 +5 wsl111 2026-03-01 5/250 2026-03-01 23:45 by 暮雨星晴
[考研] 材料化工调剂 +12 今夏不夏 2026-03-01 13/650 2026-03-01 23:32 by L135790
[考研] 材料学硕318求调剂 +5 February_Feb 2026-03-01 5/250 2026-03-01 23:31 by L135790
[考研] 265分求调剂不调专业和学校有行学上就 +6 礼堂丁真258 2026-02-28 8/400 2026-03-01 22:50 by jian_
[考研] 0856调剂 +5 刘梦微 2026-02-28 5/250 2026-03-01 22:30 by wang_dand
[考研] 材料类求调剂 +10 wana_kiko 2026-02-28 12/600 2026-03-01 22:10 by 海嵙Y
[考研] 299求调剂 +3 Y墨明棋妙Y 2026-02-28 5/250 2026-03-01 21:01 by tangxiaotian
[考研] 0856材料求调剂 +4 麻辣鱿鱼 2026-02-28 4/200 2026-03-01 16:51 by caszguilin
[考研] 307求调剂 +5 wyyyqx 2026-03-01 5/250 2026-03-01 15:21 by Fff-1
[考研] 材料工程274求调剂 +3 Lilithan 2026-03-01 3/150 2026-03-01 14:58 by ms629
[考研] 303求调剂 +4 今夏不夏 2026-03-01 4/200 2026-03-01 14:46 by 嘟嘟小浣熊
[考研] 295复试调剂 +3 简木ChuFront 2026-03-01 3/150 2026-03-01 14:27 by zzxw520th
[考研] 298求调剂 +9 人间唯你是清欢 2026-02-28 12/600 2026-03-01 14:23 by Ducount.Y
[考研] 寻找调剂 +4 LYidhsjabdj 2026-02-28 4/200 2026-03-01 10:56 by sunny81
[考研] 材料调剂 +4 爱擦汗的可乐冰 2026-02-28 4/200 2026-03-01 00:38 by 猫猫球alter
[考研] 264求调剂 +3 巴拉巴拉根556 2026-02-28 3/150 2026-02-28 21:31 by gaoxiaoniuma
[高分子] 求环氧树脂研发1名 +3 孙xc 2026-02-25 11/550 2026-02-28 16:57 by ichall
信息提示
请填处理意见