[求助]
文献求助
|
||
| 有一篇论文的参考文献是这样的A. Inoue, T. Zhang, N. Nishiyama, K. Ohba, T.Masumoto, Mater Trans. JIM 34 (in press) no.12. 我找不到这篇文章，望有线索的虫前辈们给予指点，新虫在此不胜感激。新虫初来咋到，金币少的可怜，此次几乎倾囊了，望大家不要嫌少。 |
回复此楼» 猜你喜欢
铜合金材料加工课件资源
已经有0人回复
-
一条软包电池实验线，折边机是必须配的设备吗？
已经有0人回复
-
无机非金属材料论文润色/翻译怎么收费?
已经有284人回复
-
掺杂Er3+的体系 有没有更新的测温模式？
已经有5人回复
-
静电纺丝膜厚度问题
已经有94人回复
-
软包电池极耳上点焊的焊点为什么不容易脱落？
已经有0人回复
-
常规静电纺丝制备
已经有106人回复
-
中国科学院新疆理化所招收2027年工业催化与碳材料方向“申请-考核制”博士生
已经有74人回复
-
PLLA静电纺丝辊筒出现空隙带和纺丝膜透光有圆点，求解答
已经有2人回复
-
热压化成为什么要加热还要加压？
已经有0人回复
3楼2012-06-25 16:47:42
【答案】应助回帖
感谢参与，应助指数 +1
|
http://www.jim.or.jp/journal/e/34/12/1234.html Preparation of 16 mm Diameter Rod of Amorphous Zr65Al7.5Ni10Cu17.5 Alloy A. Inoue, T. Zhang, N. Nishiyama†, K. Ohba†† and T. Masumoto Institute for Materials Research, Tohoku University, Sendai 980, Japan Bulky amorphous alloys in a cylindrical shape with diameters up to 16 mm were found to form by water quenching a Zr65Al7.5Ni10Cu17.5 melt in a quartz tube. The amorphous phase of this alloy has the widest temperature interval of supercooled liquid region before crystallization. The glass transition temperature, crystallization temperature and Vickers hardness for the bulky amorphous alloy with a diameter of 16 mm are 625 K, 750 K and 465, respectively, being nearly the same as those for the corresponding melt-spun ribbon with a thickness of 30 µm. The extremely large glassforming ability is presumably due to a combination of significantly different atomic size ratios among the constituent elements and the necessity of redistribution of Al for the progress of crystallization. The finding of the extremely large glass-forming ability has a very important implication because it demonstrates the possibility of bulk amorphous alloy production by conventional casting processes. (Received August 20, 1993) Keywords: glass-forming ability, zirconium base alloy, bulky amorphous alloy, water quenching, low critical cooling rate † On leave from Teikoku Piston Ring Co., Ltd., Okaya 394, Japan. †† Graduate Student, Tohoku University. |
» 本帖附件资源列表
-
欢迎监督和反馈：小木虫仅提供交流平台，不对该内容负责。
本内容由用户自主发布，如果其内容涉及到知识产权问题，其责任在于用户本人，如对版权有异议，请联系邮箱：xiaomuchong@tal.com - 附件 1 : Preparation of 16 mm Diameter Rod of Amorphous Zr65Al7.5Ni10Cu17.5 Alloy.pdf
2012-06-25 13:16:53, 938.83 K
2楼2012-06-25 13:17:16
4楼2012-06-25 17:08:16
5楼2012-06-25 17:56:16